中英文翻译刀具与材料.doc
攀枝花学院本科毕业设计(论文)外文译文院(系):机电工程学院专业:机械设计制造及其自动化姓名:学号:指导教师评语:签名:年月日外语文献翻译摘自:制造工程与技术(机加工)(英文版)ManufacturingEngineeringandTechnologyMachining机械工业出版社2004年3月第1版页564560P美s.卡尔帕基安(Seropekalpakjian)s.r施密德(StevenR.Schmid)著原文:20.9MACHINABILITYThemachinabilityofamaterialusuallydefinedintermsoffourfactors:1、Surfacefinishandintegrityofthemachinedpart;2、Toollifeobtained;3、Forceandpowerrequirements;4、Chipcontrol.Thus,goodmachinabilitygoodsurfacefinishandintegrity,longtoollife,andlowforceAndpowerrequirements.Asforchipcontrol,longandthin(stringy)curedchips,ifnotbrokenup,canseverelyinterferewiththecuttingoperationbybecomingentangledinthecuttingzone.Becauseofthecomplexnatureofcuttingoperations,itisdifficulttoestablishrelationshipsthatquantitativelydefinethemachinabilityofamaterial.Inmanufacturingplants,toollifeandsurfaceroughnessaregenerallyconsideredtobethemostimportantfactorsinmachinability.Althoughnotusedmuchanymore,approximatemachinabilityratingsareavailableintheexamplebelow.20.9.1MachinabilityOfSteelsBecausesteelsareamongthemostimportantengineeringmaterials(asnotedinChapter5),theirmachinabilityhasbeenstudiedextensively.Themachinabilityofsteelshasbeenmainlyimprovedbyaddingleadandsulfurtoobtainso-calledfree-machiningsteels.ResulfurizedandRephosphorizedsteels.Sulfurinsteelsformsmanganesesulfideinclusions(second-phaseparticles),whichactasstressraisersintheprimaryshearzone.Asaresult,thechipsproducedbreakupeasilyandaresmall;thisimprovesmachinability.Thesize,shape,distribution,andconcentrationoftheseinclusionssignificantlyinfluencemachinability.Elementssuchastelluriumandselenium,whicharebothchemicallysimilartosulfur,actasinclusionmodifiersinresulfurizedsteels.Phosphorusinsteelshastwomajoreffects.Itstrengthenstheferrite,causingincreasedhardness.Hardersteelsresultinbetterchipformationandsurfacefinish.Notethatsoftsteelscanbedifficulttomachine,withbuilt-upedgeformationandpoorsurfacefinish.Thesecondeffectisthatincreasedhardnesscausestheformationofshortchipsinsteadofcontinuousstringyones,therebyimprovingmachinability.LeadedSteels.Ahighpercentageofleadinsteelssolidifiesatthetipofmanganesesulfideinclusions.Innon-resulfurizedgradesofsteel,leadtakestheformofdispersedfineparticles.Leadisinsolubleiniron,copper,andaluminumandtheiralloys.Becauseofitslowshearstrength,therefore,leadactsasasolidlubricant(Section32.11)andissmearedoverthetool-chipinterfaceduringcutting.Thisbehaviorhasbeenverifiedbythepresenceofhighconcentrationsofleadonthetool-sidefaceofchipswhenmachiningleadedsteels.Whenthetemperatureissufficientlyhigh-forinstance,athighcuttingspeedsandfeeds(Section20.6)theleadmeltsdirectlyinfrontofthetool,actingasaliquidlubricant.Inadditiontothiseffect,leadlowerstheshearstressintheprimaryshearzone,reducingcuttingforcesandpowerconsumption.Leadcanbeusedineverygradeofsteel,suchas