常用金属原料性能介绍.doc

附錄三 常用金屬材料性能介紹表一. 黃銅, 鈦銅, 磷青銅性能比較定義7-3黃銅70% Cu黃黃銅65% Cu鈦銅磷青銅6%Sn彈簧用磷青銅銅編號C2600C2680TiCuR1C5191C5210化學成份 (%)Cu 70Zn 30Cu 65Zn 35Ti 3.1Cu+Ti 99.5%minSn 6 P 0.2Cu+Sn+P99.7minSn 8 P 0.2Cu+Sn+P99.7min物理性質 比重 (g/cm3)熔點范圍 (C )熱膨脹系數 (10-6/ C)彈性系數 (kgf/mm2)導電性 (%IACS)8.53915-95519.9(20-300 C)11,200288.47903-93020.3(20-300 C)10,500278.701,040-1,07018.6(30-450 C)13,000138.83890-1,04517.6(20-300 C)11,200148.80860-1,02517.6(20-300 C)11,20013機械性質 回火 0 1/4H 抗拉強度 1/2H(kgf/mm2) H EH SH30-3933-4236-4542-5553min30-3933-4236-4542-5553min80min95min32min40-5250-6260-7065min48-6260-7270-8075-85 0 1/4H 伸長率(%) 1/2H H EH SH40min35min28min-40min35min28min-15min5min42min35min20min8min5min27min20min11min9min 0 1/4H 維克式硬度 1/2H (Hv) H EH SH75-12585-145105-175145min75-12585-145105-175145min250-300300-350100-160150-205180-230200min140-205185-235210-260230-270 0彈簧的 1/4H(M) 彈性極限 1/2H(KbO-1) H(kgf/mm2) EH(M) SH-70min85min25min40min47min52min應力松馳XX 材料錫 暴露於蒸氯中OOOOO 鹽霧實驗腐蝕 暴露至二硫化 物氯體中XXOOOOO應力蝕裂性XX軟化溫度I(HV 80%)325C(30min)325C(30min)530C(60min)360C(60min)370C(60min)生產范圍厚度 mm 寬度 mm卷料重量 kg/mm0.04-3.06-6100.5-3.50.04-3.06-6100.5-3.50.06-0.86-4000.5-2.00.05-2.06-6100.5-350.05-2.06-6100.5-35可用形狀用途板材料帶,可用於汽車水箱, 連接器接頭及電燈裝置板材料帶,可用於汽車水箱, 扣子, 反射器板材料帶,可用於連接器, 開關, 繼電器及其他電子元件板材料帶可用於端子, 連接器, 電子元件的彈簧及開關導線架, 膜盒及墊片Note: : excellent O : good : average X : not good表二, 鈹銅性能介紹:定義Brush Alloy 25鈹銅合金Brush Alloy 165鈹銅合金Brush Alloy 190鈹銅合金Brush Alloy290鈹銅合金銅編號C17200C17000C17200C17200物理性質 比重 (g/cm3)熱傳導率 (W/ m. K)彈性系數 (kgf/mm2)導電性 (%IACS)降伏強度(0.01%)(kg/mm2)降伏強度 (0.2%支距)8.258513,5002274-9198-1248.308510,5001870-8591-1178.3612013,00017-8.3612011,20017- A 1/4H 完全的伸長(%) 1/2H H AT 1/4HT 1/2HT HT (TM00) AM (TM02) 1/4HM (TM04) 1/2HM (TM06) HM (TM08) HM XHM XHMS35-6020-4512-302-183-103-151-81-635-6020-4512-302-103-203-151-101-618-3015-2512-229-209-183-1016-3015-2512-229-209-184-153-1219-3514-308-255-133-15 A 1/4H 耐應力松馳性 1/2H 乘余應力% H (75%於0.2% AT 降伏強度) 1/4HT(1,000hours at 1/2HT 100C) HT (TM00) AM (TM02) 1/4HM (TM04) 1/2HM (TM06) HM (TM08) HM XHM XHMS9696979896979798979798989898979797989898989797989999 A 1/4H 疲勞強度 1/2H H (104周期) AT (R=-1) 1/4HT (kg/mm2) 1/2HT HT (TM00) AM (TM02) 1/4HM (TM04) 1/2HM (TM06) HM (TM08) HM XHM XHMS28-3228-3229-3332-35-26-3027-3128-3230-3328-3228-3230-3432-3733-3935-4028-3229-3329-3432-3633-3935-4035-4228-3229-3431-3533-4035-42 A 1/4H 成型性 1/2H H(Min. R/t對於 AT90度折彎) 1/4HT(Transverse) 1/2HT HT (TM00) AM (TM02) 1/4HM (TM04) 1/2HM (TM06) HM (TM08) HM XHM XHMS00130013-00.5135700.51224600123表三. 不銹鋼系列性能介紹:品種沃思田系不銹鋼品種記號(JIS)SUS304SUS304LSUS302SUS301SUS310SSUS321化學成份 (%)C 0.08Si 1.0Mn 2.0P 0.045S 0.03Ni 8.010.5Cr 18.020.0Fe 殘部C 0.03Si 1.0Mn 2.0P 0.045S 0.03Ni 9.013.0Cr 16.018.0Fe 殘部C 0.15Si 1.0Mn 2.0P 0.045S 0.03Ni 8.010.0Cr 17.019.0Fe 殘部C 0.15Si 1.0Mn 2.0P 0.045S 0.03Ni 6.08.0Cr 16.018.0Fe 殘部C 0.08Si 1.5Mn 2.0P 0.045S 0.03Ni 19.022.0Cr 24.026.0Fe 殘部C 0.08Si 1.0Mn 2.0P 0.045S 0.03Ni 9.013.0Cr 17.019.0Ti 5*C%以上Fe 殘部物理性質 比重 (g/cm3)熔融溫度 (C )熱膨脹系數(10-4/ C) 20-100C 20-300C熱傳導度導電率(%IASat 20C)退火溫度 (C)消除應力退火溫度(C)8.031399-145417.318.70.03881010-1150急冷350-4508.031399-145417.318.70.03881010-1150急冷350-4508.031399-142117.318.70.03881010-1150急冷350-4508.031399-142116.918.70.03881010-1150急冷350-4508.031399-145414.417.50.03301030-1180急冷350-4508.031399-142716.719.30.0384920-1150急冷350-450機械性質 質 別*1抗拉強度 (kgf/mm2)*2伸長率 (%)*3VICKERS Hv(退火狀態時的值)彈性系數 (E) (kgf/mm2) O 1/2H 3/4H H53 80 95 11540 6 3 200 250 310 3701970004940200197000534020019700O 1/2H 3/4H H EH53 .95. 115 135 16040 10 10 200 310 370 430 49019700053402002040005340MnNi提高CrMnNi回火抵抗弱Cr Si MnNi固熔后使肥粒鐵強化韌性MoMnNi1. 脫酸劑2. 由硫來防脆3. 增加淬火性4. 耐磨耗, 耐沖擊鋼5. Ni代用不銹鋼P微弱稍高時易裂回火抵抗稍增固熔化顯著硬化, 脆化也大1. 回火形成脆化的原因2. 熔融流動性變好3. 耐腐性變強4. 快削鋼增加可削性S無特別影響, 易裂1. 白熱, 赤熱脆性的原因2. 硫磺快削鋼(0.10.3%S)3. 非金屬介在物生成Cr相當強WCrMn大防止稍軟化稍硬化1. 耐銹, 耐酸化性增加大2. 高溫強度增加(耐熱鋼)3. 高C耐磨耗性增大(軸受鋼)4. 增加淬火性NiFeNi稍高, 碳含量會殘留沃斯田鐵回火抵抗性無稍硬化, 韌性增加1. 退火狀態強, 韌性增加2. 炭素鋼低溫韌性增加3. 在高Cr-Fe合金添加沃斯田鐵系不銹鋼4. 高Ni-Fe合金 permalloy 40-80%Ni)Cu稍高Ni的一半程度無回火抵抗性(450-600C析出硬化)1. 耐腐蝕性增加2. 低合金鋼強度增加3. Cu多時發生赤熱脆化4. 時效現象發生W相當強即使少量也相當大回火抵抗大二次硬化大顯著硬化及時效硬化1. 高溫強度顯著提高(高速度鋼)2. 因特殊炭化物耐磨耗性增加3. 磁石鋼(1-10%W)Mo強Mo Cr大(固熔時Mo Cr)增加脆性防止回火抵抗 大二次硬化 大強韌性增加1. 提高沃斯田鐵粒的生長速度2. 高溫chip限, 提高赤熱, 常溫強度3. 防回火脆性4. 耐蝕性增加5. 淬火性增加V強Ti, Cb V Mn固熔時相當大回火抵抗 大二次硬化 最大稍硬化1. 高溫強度提高2. 炭化物微細化3