钛白粉成分表.doc

titanium dioxide 钛白粉Rutile 金红石94%Product name: titanium dioxideMolecular formula: TiO2CAS No.: 13463-67-7Appearance: white powderUse: paint, ink etc.ParametersAnalysis resultTiO94.5%White degree ( contrast to the standard sample )99%Tint reducing power ( contrast to the standard sample )100%Volatile content ( 105Cafter 23C, 24h )0.45%Water soluble matter0.4%Oil absorption22g/100gpH vaule7.0Resistivity in water extraction32Residue on sieve 45m0.8%98%Specifications:ItemSpecificationTiO2Content/% 98.0Volatile at 105 /%0.5Water Soluble Objects /%0.6Tint Reducing Power100PHValue of Aqueous Suspension6.58.5Oil Absorption (g/100g)24Scattering power105Colorwith no less than than the standard sampleHiding power 30Achromatic, and with the standard 100Specification 金红石98%ItemIndexTitanium Dioxide Content, %95.0Rutile Content, %98.0Whiteness, %Tinter reducing power, compared with standard samples98105C volatile matter, %0.5Water solubles, %0.3pH-value of aqueous suspension6.5-7.5Oil absorption, g/ 100g22Residue on sieve 45m, %0.05Resistivity of aqueous extract, .cm8000RutileTitanium Dioxide(Normal use): 金红石Surface treament:Silicon, Aluminium and OrganicIndex Name:Grade oneTiO2%min:92.50%Rutile conversion rate min:97%Color(compared with sample):Not lowerWhiteness min:96Achromaticity(compared with sample), % min:100Dispersion(hagerman number)min:6.0105 centidegree Volatile matter, % max:0.5Sileve Residue per 45um mesh, % max:0.02Water Solubles, % max:0.5pH of Suspension Solution:6.5-8.5Oil Absorption g/100g max:22锐太 AnataseTitanium Dioxide(Normal use):Index Name:Grade oneTiO2%min:98.00%Color(compared with sample):Not lowerAchromaticity(compared with sample), % min:100105 centidegree Volatile matter, % max:0.5Water Solubles, % max:0.5pH of Suspension Solution:6.5-8.0Oil Absorption g/100g max:26Sileve Residue per 45um mesh, % max:0.1Water extract resistivity Ω M min.:20锐太 B101-BITEM : anatase titanium dioxide B101-BPackage : 25 kg/ woven bag2. SpecificationNoitemUnitResults1Content of Active TiO2 and Assistant%982White degree (contrast to the standard sample)%similar3Tint reducing power(contrast to the standard sample)%1004Oil absorptiong/100g235PH Val