VAE、不饱和聚酯、干燥剂Universal milky glue.doc

Universal milky glue CN 102220095 B 摘要摘要 翻译自中文 Of the present invention are non toxic white glue adhesive technology Component has a VAE emulsion unsaturated polyester resins rare earth driers their mass ratio is 100 0 to 20 0 to 0 12 unsaturated polyester resin and a rare earth driers are not simultaneously 0 The present invention is non toxic white glue fast drying are fast rubber non toxic and tasteless does not pollute the environment to ensure that the operator s physical and mental health has strong adhesive strength may be appropriately diluted with water without compromising quality with a storage stable sex can be used for bonding glass ceramics stone wood concrete metal etc as well as interior decoration 权利要求权利要求 4 翻译自中文 1 a non toxic white glue the vinyl acetate vinyl emulsion polymerization unsaturated polyester resins rare earth composition driers vinyl acetate vinyl emulsion polymerization unsaturated polyester resin and a rare earth driers at a mass ratio of 100 O 20 O 0 12 unsaturated polyester resin and a rare earth driers are not both O 2 as claimed in claim 1 wherein the non toxic white glue characterized in that when the vinyl acetate ethylene copolymer emulsion and unsaturated polyester resin by mass ratio is 100 15 to 20 or a vinyl acetate vinyl emulsion polymerization is not unsaturated polyester resins and driers earth mass ratio of 100 15 to 20 0 12 obtained from dry white glue 3 according to claim 1 wherein the non toxic white glue characterized in that when the vinyl acetate ethylene copolymer emulsion and a rare earth driers at a mass ratio of 100 0 08 to 0 1 or a vinyl acetate vinyl emulsion polymerization unsaturated polyester resins and rare earth driers mass ratio of 100 10 15 0 1 to 0 12 you get quick drying white glue As claimed in claim 1 2 or 3 wherein the non toxic white glue characterized in that said vinyl acetate vinyl polymer emulsions are emulsions or VAE 707 VAE 705 emulsion said unsaturated polyester resin is Saturated polyester resin 191 说明说明 翻译自中文 Non toxic white glue Technology 0001 The present invention belongs to the technical field of the adhesive the adhesive involves a green chemical products BACKGROUND 0002 Adhesive divided into two categories one is a solvent based adhesives and the other is a water based adhesive Solvent based adhesives is rubber plastics and other substances dissolved in benzene solvent to dissolve it becomes solvent based adhesives Solvent based adhesives short fastness large fast drying but highly toxic long term benzene solvent release in the environment it will cause pollution of the environment on the human body injury physical injury on the decor is the largest can cause cancer and cause many other diseases so no matter in any field are undesirable White gum is a water based adhesives such as vinyl acetate synthetic esters i e vinyl acetate such a plastic non toxic but the strength difference is not waterproof water a plastic foam to open and the drying speed is too slow the ability to 24 hours so that the sticky then the field is rarely used now mainly used as a coating to reconcile agent 0003 with the present invention proximity technology is now on the market of the 801 classic plastic or wood its constituent components are rubber plastic and other substances This glue is used in interior decoration the harm caused by its toxic is quite large the release of benzene poisoning workers on the operation is almost unbearable and bonding time with fastness 3 to 5 years On almost all collapse SUMMARY OF THE INVENTION 0004 The present invention solves the technical problem is that the open a non toxic white glue environmentally friendly non toxic and very strong adhesive fastness 0005 The present invention there are two types of non toxic white glue from the dry type 2 drying type Because the use of a wide range of so called universal white glue 0006 The present invention specific technical programs are 0007 toxic colors white glue component has a vinyl acetate ethylene copolymer emulsion VAE emulsion unsaturated polyester resin months purpose rare earth driers vinyl acetate vinyl emulsion polymerization unsaturated polyester resin and driers earth mass ratio of 100 O 20 O 0 12 unsaturated polyester resin and a rare earth driers are not both O 0008 When vinyl acetate ethylene copolymer emulsion and unsaturated polyester resin by mass ratio is 100 15 to 20 or a vinyl acetate vinyl emulsion polymerization unsaturated polyester resin and a rare earth driers at a mass ratio of 100 15 to 20 0 12 you get from dry white glue 0009 When vinyl acetate ethylene copolymer emulsion and a rare earth driers at a mass ratio of 100 0 08 to 0 1 or a vinyl acetate vinyl emulsion polymerization unsaturated polyester resin and a rare earth driers at a mass ratio of 100 10 to 15 0 1 to 0 12 you get quick drying white glue 0010 The present invention is the preparation of non toxic white glue process according to the component ratio of the unsaturated polyester resin is added to the VAE emulsion and mixed uniformly and then adding rare earth driers stir 0011 The present invention is vinyl acetate vinyl emulsion polymerization can be selected Beijing Organic Chemical Plant VAE 705 emulsions or VAE 707 emulsion unsaturated polyester resin may be used any manufacturer of products on the market may be for example unsaturated polyester resin 191 cheap Rare driers can choose Gushan up chemical products 0012 The present invention VAE emulsion with excellent overall performance water resistant low temperature deposition acid etc can be miscible with many materials Rare driers advent of the 1990s non toxic and efficient driers does not contain lead cobalt harmful substances a new non toxic and convenient storage Unsaturated polyester resins flavored non toxic less used in the present invention to improve overall performance 0013 The present invention is from dry white adhesive bonding strength for bonding glass ceramics stone wood cement metal etc quick drying white glue mainly used for indoor decoration Whether it is self drying white glue or quick drying white glue using the method is the same you can glue bond will be binding coincidence You can also glue to dry after a little time and then will be binding coincidence so white glue dries quickly is binding bonding firm After the glue drying time with the prior art are similar with the season the ambient temperature is different from the master of their own operator 0014 The present invention is non toxic white glue fast drying air drying time of 5 to 20 minutes and wood glue dry at a fairly classic is fast rubber non toxic and tasteless does not pollute the environment to ensure the health of the operator has strong adhesive strength use of personnel with experience in the trial said the firm level bonding is stronger than wood vintage plastic may be appropriately diluted with water without compromising quality with a storage stability can be used for bonding glass ceramics stone wood concrete metal etc as well as interior decoration In summary the present invention is non toxic white glue is a variety of properties on the market now than solvent based glue wide range of applications is non toxic green chemical products Specific embodiments 0015 Example 1 0016 100 parts by mass of VAE 707 the emulsion was added 20 parts by mass of an unsaturated polyester resin 191 obtained from mixed dry white glue 0017 Example 2 0018 100 parts by mass of VAE 707 emulsion adding 15 to 20 parts by mass of an unsaturated polyester resin 191 mixed then added 0 12 parts by mass of a rare earth driers stir to obtain self dry white glue 0019 Example 3 0020 100 parts by mass of VAE 705 the emulsion was added 15 parts by mass of an unsaturated polyester resin 191 obtained from mixed dry white glue 0021 Example 4 0022 100 parts by mass of VAE 705 the emulsion was added 15 parts by mass of an unsaturated polyester resin 191 mixed then added 0 12 parts by mass of a rare earth driers stir obtained from dry white glue 0023 Example 5 0024 100 parts by m