破坏型测量系统分析报告

,,,MSA分析报告,,,,,,

,,,,,,,,,,

零件号和名称,,,,量具名称,万能试验机,,日期,"Saturday,July23,2016",

量具/测试方法名称,,拉伸强度,测试,量具号,P-QA08,,分析人,周A,

规范,,90MPa以上,,量具类型,强度,,确认人,王某亮,

原始数据,,,,,,,,,

,,,,,,,,,,

序号,拉伸,测试员,序号,拉伸,测试员,序号,拉伸,测试员,

1,138.3,周A,11,134.5,范C,6,142.1,周A,

2,128.0,张B,12,128.5,周A,7,136.6,张B,

3,134.9,范C,13,130.0,范C,8,137.1,范C,

4,136.3,张B,14,134.5,周A,9,104.9,周A,

5,138.3,范C,15,138.3,张B,10,116.9,张B,

6,138.3,周A,1,141.8,周A,11,130.8,范C,

7,134.7,张B,2,130.7,张B,12,128.3,周A,

8,139.4,范C,3,137.4,范C,13,135.2,范C,

9,106.8,周A,4,135.0,张B,14,129.7,周A,

10,111.9,张B,5,137.7,范C,15,141.8,张B,

,,,,,,,,,,

分析结果,,,,,,,,,

量具R&R研究-嵌套方差分析,,,,,,,,,

拉伸强度,的量具R&R（嵌套）,,,,,,,,

量具名称:万能试验机,,,,,,,,,

研究日期:2016/7/23,,,,,,,,,

报表人:周A,,,,,,,,,

公差:0.01MPa,,,,,,,,,

其他:,,,,,,,,,

,,,,,,,,,,

测试数据的量具R&R（嵌套）,,,,,,,,,

,,,,,,,,,

来源自由度SSMSFP,,,,,,,,,

测量员2207.12103.5610.50660.615,,,,,,,,,

序号(测量员)122453.07204.42339.15420.000,,,,,,,,,

重复性1578.315.221,,,,,,,,,

合计292738.51,,,,,,,,,

,,,,,,,,,

,,,,,,,,,

量具R&R,,,,,,,,,

,,,,,,,,,,

方差分量,,,,,,,,,

来源方差分量贡献率,,,,,,,,,

合计量具R&R5.2214.98,,,,,,,,,

重复性5.2214.98,,,,,,,,,

再现性0.0000.00,,,,,,,,,

部件间99.60195.02,,,,,,,,,

合计变异104.822100.00,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

过程公差下限=90,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

研究变异%研究变%公差,,,,,,,,,

来源标准差(SD)(6

*

SD)异(%SV)(SV/Toler),,,,,,,,,

合计量具R&R2.284913.709722.3216.34,,,,,,,,,

重复性2.284913.709722.3216.34,,,,,,,,,

再现性0.00000.00000.000.00,,,,,,,,,

部件间9.980059.880297.4871.35,,,,,,,,,

合计变异10.238361.4295100.0073.20,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

可区分的类别数=6,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

,,,,,,,,,,

"拉伸强度的量具R&R（嵌套）：

1、合计量具R&R贡献率：4.98%，小于10%，表明测量系统可接受。

2、来自部件间的贡献百分比(95.02)大于合计量具R&R的贡献百分比(4.98)。这表明大部分变异是由于部件间的差异所致。

3、合计量具R&R%研究变异：16.34%，小于30%，表明测量系统有条件接受。需考虑具体应用、测量设备成本、维修成本或其他