附件2-1 腐蚀风险研究表

附件2-3腐蚀风险研究表汇总表3-1原料油工段腐蚀风险研究表回路编号回路起止点/设备编号(部位）温度（℃）压力（MPa）腐蚀介质含量材质潜在损伤机理（主要机理加粗）损伤类型影响因素腐蚀速率(mm/a)/敏感性风险评估失效可能性失效后果风险等级CCHL01-G1-01原料油→V1201→P1201/A,B→E1204/A,B壳程→E1208壳程→E1216/A~F壳程→E1214/A,B壳程前80~1800.2~1.55硫含量0.7420#2-湿硫化氢腐蚀开裂/减薄硫化氢含量、温度、pH值、材料低1B低风险V120180~1100.2~1.55硫含量0.74%Q345R2-湿硫化氢腐蚀开裂/减薄硫化氢含量、温度、pH值、材料低1B低风险E1204/A,B管束外侧、E1208管束外侧、E1216/A~F管束外侧80~1800.2~1.55硫含量0.74%10#2-湿硫化氢腐蚀开裂/减薄硫化氢含量、温度、pH值、材料低1B低风险CCHL01-G1-02原料油自E1214/A,B壳程至混合器再至R1101A2251.25硫含量酸值0.74%0.62mgKOH/g20#1-高温硫腐蚀减薄硫含量、温度、流速0.151B低风险6-环烷酸腐蚀减薄酸值、温度、硫含量、流速0.151B低风险20-冲蚀/冲蚀-磨蚀减薄流速与流向0.151B低风险E1214/A,B壳程2251.25硫含量酸值0.74%0.62mgKOH/gQ345R1-高温硫腐蚀减薄硫含量、温度、流速0.031B低风险6-环烷酸腐蚀减薄酸值、温度、硫含量、流速0.031B低风险20-冲蚀/冲蚀-磨蚀减薄流速与流向0.031B低风险CCHL01-G1-03回炼油→V1201/V12023290.2硫含量/20#1-高温硫腐蚀减薄硫含量、温度、材料0.101B低风险20-冲蚀/冲蚀-磨蚀减薄流速与流向0.101B低风险V1202→回炼油原料油混合线3231.25硫含量/1Cr5Mo1-高温硫腐蚀减薄硫含量、温度、材料0.101B低风险20-冲蚀/冲蚀-磨蚀减薄流速与流向0.101B低风险V12023290.2硫含量/Q345R+S321681-高温硫腐蚀减薄硫含量、温度、材料0.081B低风险20-冲蚀/冲蚀-磨蚀减薄流速与流向0.081B低风险表3-2反再及外取热工段腐蚀风险研究表回路编号回路起止点/设备编号(部位）温度（℃）压力（MPa）腐蚀介质含量材质潜在损伤机理（主要机理加粗）损伤类型影响因素腐蚀速率(mm/a)/敏感性风险评估失效可能性失效后果风险等级CCHL01-G2-01提升管反应器再生斜管再生滑阀5500.2催化剂、硫硫：0.74%Q245R+衬里14-耐火材料退化材质裂化设计、施工、工艺环境中风险20-冲刷腐蚀/磨蚀减薄固体颗粒、流速中风险12-热疲劳开裂温度波动幅度和频率、应力、循环次数、开停车频率中风险1-高温硫腐蚀减薄硫含量、温度、合金成分低风险15-石墨化材质劣化材料、应力、温度、时间低风险33-475℃脆化材质劣化合金成分、应力、温度低风险5-连多硫酸腐蚀（开停工）开裂硫化物、水、材料敏化、应力低风险CCHL01-G2-02同轴式沉降器-再生器壳体外取热器壳体预冷器壳体7000.2催化剂、SO2、SO3、NO2、NO3/Q245R+衬里14-耐火材料退化材质裂化设计、施工、工艺环境中风险20-冲刷腐蚀/磨蚀减薄固体颗粒、流速中风险12-热疲劳开裂温度波动幅度和频率、应力、循环次数、开停车频率中风险3-蠕变开裂材料、应力、温度低风险A-硝酸盐应力腐蚀开裂开裂合金成分、含碳量、温度低风险内构件30432-σ相脆化材质劣化合金成分、投用年限、温度低风险14-耐火材料退化材质裂化设计、施工、工艺环境中风险20-冲刷腐蚀/磨蚀减薄固体颗粒、流速中风险54-机械疲劳开裂振动频率、应力、循环次数、材料性能低风险12-热疲劳开裂温度波动幅度和频率、应力、循环次数、开停车频率低风险24-碳化材质裂化渗碳环境、温度低风险5-连多硫酸腐蚀（开停工）开裂硫化物、水、材料敏化、应力低风险23-氯应力腐蚀开裂开裂氯化物含量、温度、pH、拉应力、氧、合金成分低风险膨胀节316H5-连多硫酸腐蚀（开停工）开裂硫化物、水、材料敏化、应力低风险23-氯应力腐蚀开裂开裂氯化物含量、温度、pH、拉应力、氧、合金成分低风险12-热疲劳开裂温度波动幅度和频率、应力、循环次数、开停车频率中风险表3-3烟气工段腐蚀风险研究表回路编号回路起止点/设备编号(部位）温度（℃）压力（MPa）腐蚀介质含量材质潜在损伤机理（主要机理加粗）损伤类型影响因素腐蚀速率(mm/a)/敏感性风险评估失效可能性失效后果风险等级CCHL01-G3-01自再生器烟气集合管到三级旋风分离器（CY1104）6840.23烟气催化剂20#+衬里耐火材料退化材质劣化开裂烧焦温度、催化剂含量、设备外壁温度/1B低冲蚀磨蚀减薄/1B低S30409冲蚀磨蚀减薄0.022A低三级旋风分离器（CY1104）内构件热疲劳材质劣化/1B低σ相脆化材质劣化温度、使用时间/2B低CCHL01-G3-02三级旋风分离器（CY1104）出口至烟气轮机出口675-5150.21烟气催化剂316H冲刷腐蚀减薄烟气浓度、催化剂含量0.033B低膨胀节氯应力腐蚀开裂开裂/3B低烟气露点腐蚀、连多硫酸腐蚀（开停工）减薄、开裂0.033B低CCHL01-G3-03烟气轮机出口到水封罐5150.2烟气催化剂20#+衬里耐火材料退化材质劣化开裂烟气浓度/1B低三级旋分器双动滑阀至CO炉入口681四旋烟气至CO炉入口358冲蚀减薄/1B低四旋分离器V1107再生烟气临界流速喷嘴350S30409冲蚀减薄0.033B低水封罐515CCHL01-G3-04CO炉至余热锅炉炉壁577-4170.0006烟气催化剂20#+衬里衬里耐火材料材质劣化开裂烟气浓度外壁温度/1B低水保护炉管外侧高温过热段炉管外侧低温过热段炉管外侧蒸发段炉管外侧20G冲蚀减薄0.0251A低12Cr1MoVG/06Cr19Ni10蠕变材质劣化/1B低12Cr1MoVG/06Cr13石墨化材质劣化/1B低20G球化材质劣化/1B低CCHL01-G3-05脱硝系统E1901气气换热器管外侧417-2880.0006烟气催化剂氨水20冲蚀减薄烟气浓度0.0251A低I1901喷氨格栅20G3901整流装置Q235BCCHL01-G3-06余热锅炉省煤器炉管外侧288-187烟气催化剂20G/08Al烟气露点腐蚀减薄排烟温度0.0251C中冲蚀0.0251A低CCHL01-G3-07余热锅炉出口至分离股管线187-60烟气浆液20烟气露点腐蚀减薄烟气温度0.0251A低文丘里洗涤器J-1701A/BS31608硫酸腐蚀减薄烟气浓度0.0251A低D1701分离股气相S31608冲蚀/磨蚀减薄固含量、流速0.0251A低CCHL01-G3-08D1701液相出口至外排50常压浆液碱液碳钢碱腐蚀减薄废水pH值0.0251A低E1801/A,BS31608V1801V1805碳钢+涂料冲蚀/磨蚀减薄固含量、流速0.0251A低V1802AB碳钢+涂料CCHL01-G3-09吹灰器瓦斯线300.1瓦斯碳钢湿硫化氢腐蚀开裂/减薄瓦斯成分低1C中酸性水腐蚀减薄瓦斯成分0.253C中表3-4分馏工段腐蚀风险研究表回路编号回路起止点/设备编号(部位）温度（℃）压力（MPa）腐蚀介质含量材质潜在损伤机理（主要机理加粗）损伤类型影响因素腐蚀速率(mm/a)/敏感性风险评估失效可能性失效后果风险等级CCHL01G4-01反应油气→T1201519H2H2S7%1.19%20#+衬里3-蠕变材质裂化材料、载荷、温度低1E中高风险15-石墨化材质裂化化学组成、应力、温度、暴露时间低1E中高风险1-高温硫腐蚀减薄硫含量、流速1.701E中高风险12-热疲劳开裂温度变化低1E中高风险20-冲蚀减薄流速、固体颗粒物含量低2E中高风险CCHL01G4-02分馏塔顶油气自T1201→E1201壳程→E1202→E1203壳程→V1203122-440.16H2H2S7.43%1.50%A204B/20#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物中2D中风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1D中风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水3D中高风险13-酸性水腐蚀减薄H2S浓度、pH值、杂质、流速0.554D中高风险E1201A~D管束（外侧）1220.16H2H2S7.43%1.50%30423-氯化物应力腐蚀开裂开裂温度、浓度、pH值、应力、选材、溶解氧高5A中高风险E1201A~D壳体1220.16H2H2S7.43%1.50%Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1B低风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水3B低风险13-酸性水腐蚀减薄H2S浓度、pH值、杂质、流速4B中风险E1202A~H1220.16H2H2S7.43%1.50%Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1C中风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水2C中风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物3C中风险E1203A~D管束（外侧）440.16H2H2S7.43%1.50%304/31623-氯化物应力腐蚀开裂开裂温度、浓度、pH值、应力、选材、溶解氧中3A低风险E1203A~D壳体440.16H2H2S7.43%1.50%Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1B低风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物3B低风险V1203（封头）440.16H2H2S7.43%1.50%Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1B低风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011B低风险V1203（筒体）440.16H2H2S7.43%1.50%Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1B低风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011B低风险V1203（液包筒体）440.16H2H2S7.43%1.50%Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1B低风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011B低风险V1203（液包封头）440.16H2H2S7.43%1.50%Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险21-碳酸盐应力腐蚀开裂开裂应力、pH值和碳酸盐浓度、氰化物、H2S浓度、CO2浓度低1B低风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011B低风险CCHL01G4-03富气自V1203→V1301440.16H2H2S12.86%2.48%20#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物0.011E中高风险CCHL01G4-04酸性水自V1203→P1203→E13014420#7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物5C中高风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物中2C中风险CCHL01G4-05粗汽油自V1203→P1202→E1218壳程→T130144H2H2S0.01%0.41%20#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1218（壳体）44H2H2S0.01%0.41%Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1218（管束外侧）44H2H2S0.01%0.41%10#+内防腐2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险CCHL01G4-06顶循环油自T1201→P1204→E1204管程→E1205壳程→E1220→T1201154-8920#8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.454C中高风险T201塔顶部分154~1220.16Q245R+S113488-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251B低风险V120789Q245R13-酸性水腐蚀减薄H2S浓度、pH值、杂质、流速0.031E中高风险E1204AB（管箱）154Q345R8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.081E中高风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险E1204AB（管束内侧）15410#8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.031A低风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1205AB（壳程）154Q345R8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251A低风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险E1205AB（管束外侧）15410#8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251A低风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1220AB89Q245R8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水/4C中高风险CCHL01G4-07轻柴油自T1201→T1202→P1205→E1208管程→E1209管程；T1202→T1201206~121；20620#8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.454C中高风险轻柴油自E1209管程→E1210壳程→E1212壳程→T1303；E1210壳程→E1211→出装置；富吸收油自T1303→E1209壳程→T1202→T1201121~43；121~80；80~12120#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水/1C中风险T1201轻柴部分、V1211、V1212206~1540.16Q245R+S113488-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251C中风险T1202206~Q245R+S113488-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251C中风险E1208（管箱）206Q345R8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251C中风险E1208（管束内侧）20610#8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251A低风险E1209（管箱）Q245R8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.031B低风险E1209（管束内侧）10#8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.031A低风险E1210（壳体）Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251B低风险E1210（管束外侧）10#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.081A低风险E1212（壳体）43Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.0251B低风险E1212（管束外侧）4310#内防腐2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水0.011A低风险E1211Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险8-氯化铵腐蚀减薄NH3、HCl、H2O或铵盐浓度、温度、水1B低风险E1209（壳体）121Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险E1209（管束外侧）12110#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险CCHL01G4-08重柴油自T1201→T1203→P1207→E1213260~1Cr5Mo1-高温硫腐蚀减薄硫含量、流速/1C中风险一中油自T1201→P1206→E1313管程→E1206管程→T1201248~21920#1-高温硫腐蚀减薄硫含量、流速0.685C中高风险T1201重柴及一中循部分260~2190.16Q245R+S113481-高温硫腐蚀减薄硫含量、流速0.0251B低风险T1203260~Q245R+S113481-高温硫腐蚀减薄硫含量、流速0.0251B低风险E1313（管箱）285Q345R1-高温硫腐蚀减薄硫含量、流速0.0251D中风险E1313（管束内侧）285316L1-高温硫腐蚀减薄硫含量、流速0.0251A低风险E1206（管箱）219Q345R1-高温硫腐蚀减薄硫含量、流速0.051D中风险E1206（管束内侧）21910#1-高温硫腐蚀减薄硫含量、流速0.051A低风险CCHL01G4-09T1201→V1202→P1208→E1207管程→T1201；P1208→T1201；P1208→R1101A324~287；324；32420#；1Cr5Mo1-高温硫腐蚀减薄硫含量、流速0.102C中风险20-冲蚀减薄流速、固体颗粒物含量0.0251C中风险T1201回炼油部分360~2870.16Q245R+S113481-高温硫腐蚀减薄硫含量、流速0.0251B低风险V1202（顶封头）324Q245R+Q345R+S11348(S32168)1-高温硫腐蚀减薄硫含量、流速0.0251B低风险20-冲蚀减薄流速、固体颗粒物含量0.0251B低风险V1202（筒体）324Q245R+Q345R+S11348(S32168)1-高温硫腐蚀减薄硫含量、流速0.0251B低风险20-冲蚀减薄流速、固体颗粒物含量0.0251B低风险V1202（底封头）324Q245R+Q345R+S11348(S32168)1-高温硫腐蚀减薄硫含量、流速0.0251B低风险20-冲蚀减薄流速、固体颗粒物含量0.0251B低风险E1207（管箱）287Q345R+S321681-高温硫腐蚀减薄硫含量、流速0.0251D中风险20-冲蚀减薄流速、固体颗粒物含量0.0251D中风险E1207（管束内侧）287S321681-高温硫腐蚀减薄硫含量、流速0.051A低风险20-冲蚀减薄流速、固体颗粒物含量0.0251A低风险CCHL01G4-10油浆自T1201→P1209→E1214管程→E1215管程→T1201；T1201→T1201；P1210→E1216→E1217326~286；326；286~88.51Cr5Mo20-冲蚀减薄流速、固体颗粒物含量1.135C中高风险1-高温硫腐蚀减薄硫含量、流速1C中风险T1201塔底部分420~3600.16Q245R+S113481-高温硫腐蚀减薄硫含量、流速0.0251C中风险P1209AB32620-冲蚀减薄流速、固体颗粒物含量4E高风险E1214AB（管箱）326Q345R20-冲蚀减薄流速、固体颗粒物含量3D中高风险1-高温硫腐蚀减薄硫含量、流速0.152D中风险E1214AB（管束内侧）32630420-冲蚀减薄流速、固体颗粒物含量3A低风险1-高温硫腐蚀减薄硫含量、流速0.0251A低风险E1215A~C（管箱）303Q345R20-冲蚀减薄流速、固体颗粒物含量3D中高风险1-高温硫腐蚀减薄硫含量、流速0.061D中风险E1215A~C（管束内侧）3031020-冲蚀减薄流速、固体颗粒物含量3A低风险1-高温硫腐蚀减薄硫含量、流速0.061A低风险E1216A~F（管箱）286Q345R20-冲蚀减薄流速、固体颗粒物含量3D中高风险1-高温硫腐蚀减薄硫含量、流速0.283D中高风险E1216A~F（管束内侧）2861020-冲蚀减薄流速、固体颗粒物含量3A低风险1-高温硫腐蚀减薄硫含量、流速0.283A低风险CCHL01G4-11V1203→V1301→S1302→B1104→火炬；V1301→B1104；V1301→P1301→凝缩油41；41；410.14；0.14；0.1420#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险V1301（顶封头）410.14Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险V1301（筒体）410.14Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险V1301（底封头）410.14Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险S1302（顶封头）410.14Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险S1302（筒体）410.14Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险S1302（底封头）410.14Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险CCHL01G4-12富气自B1104→C1301→V1311→B1104→E1301→E1302壳程→V1302→酸性水出装置；气液分离罐→P1302→凝缩油；V1302→P1303→T130281~40；41；400.52；0.52；0.5120#7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.44E高风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险C1301（管箱）810.5230423-氯化物应力腐蚀开裂开裂温度、浓度、pH值、应力、选材、溶解氧中3A低风险C1301（管束内侧）810.52316L23-氯化物应力腐蚀开裂开裂温度、浓度、pH值、应力、选材、溶解氧中3C中风险V1311410.51Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物低1E中高风险E1301A~D550.51107-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.44C中高风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物中3C中风险E1302AB（壳体）450.51Q245R7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.021E中高风险2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险E1302AB（管束外侧）450.5130423-氯化物应力腐蚀开裂开裂温度、浓度、pH值、应力、选材、溶解氧中3A低风险V1302（封头）400.51Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011E中高风险V1302（筒体）400.51Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011E中高风险V1302（液包筒体）400.51Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011A低风险V1302（液包封头）400.51Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.011A低风险CCHL01G4-13V1302→T1301400.5120#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险CCHL01G4-14轻柴油→V1206→P1211→封油20#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物1B低风险V1206（封头）Q235R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物1B低风险V1206（筒体）Q235R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物1B低风险表3-5吸收稳定工段腐蚀风险研究表回路编号回路起止点/设备编号(部位）温度（℃）压力（MPa）腐蚀介质含量材质潜在损伤机理（主要机理加粗）损伤类型影响因素腐蚀速率(mm/a)/敏感性风险评估失效可能性失效后果风险等级CCHL01G5-01V1302→T1301→T1303；T1301→P1305→E1303壳程→T1301；T1301→P1306→E1304壳程→T1301；T1301→P1304→E130240；42~33；35~33；4520#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.75C中高风险T1301（顶封头）35~45Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1301（筒体）35~45Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1301（底封头）35~45Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1303AB（壳体）33Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1303AB（管束外侧）3330423-氯化物开裂开裂温度、浓度、pH值、应力、选材、溶解氧中3A低风险E1304AB（壳体）33Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1304AB（管束外侧）3310+内防腐2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险CCHL01G5-02T1303→S1302→干气出装置；T1303→E1209；S1302→E120938~4920#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低2C中风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.334C中高风险T1303（顶封头）49Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1303（筒体）49Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1303（底封头）49Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险S1302（顶封头）38Q2452-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险S1302（筒体）38Q2452-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险S1302（底封头）38Q2452-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险CCHL01G5-03V1302→T1302→E1301；V1302→E1306壳程→T1302；T1302→E1312壳程→T1302；T1302→P1307→E1305壳程41~55；41~94；123~133；1231.1520#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.835C中高风险T1302（顶封头）55~1231.15Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1302（筒体）55~1231.15Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1302（底封头）55~1231.15Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1312（壳体）1331.15Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1312（管束外侧）1331.15316L23-氯化物开裂开裂温度、浓度、pH值、应力、选材、溶解氧中3A低风险E1305（壳体）1241.15Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1305（管束外侧）1241.1510#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1306（壳体）941.15Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1B低风险E1306（管束外侧）941.1510#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险CCHL01G5-04E1305→T130412420#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1304（顶封头）56~137Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1D中风险T1304（筒体）56~137Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险T1304（底封头）56~137Q245+S113482-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险CCHL01G5-05T1304→E1310→E1311壳程→V1303→酸性水出装置；T1304→V1303→干气出装置63~33；63~3320#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物1.185E高风险E1310A~H63Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物4E高风险E1311A~H（壳体）54Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险E1311A~H（管束外侧）5430423-氯化物开裂开裂温度、浓度、pH值、应力、选材、溶解氧中3A低风险V1303（封头）33Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险V1303（筒体）33Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1E中高风险V1303（液包筒体）33Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险V1303（液包封头）33Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险CCHL01G5-06V1303→P1308→T1304；P1308→液化石油气出装置33~35；3520#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物中2E高风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.685E高风险CCHL01G5-07E1305管程→E1306管程→E1315壳程→E1307壳程→E1308→E1309壳程→P1309→E1314壳程→T1301179~3320#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险7-硫氢化铵腐蚀减薄pH值、硫氢化铵浓度、温度、氰化物0.334C中高风险E1305（管箱）179Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1305（管束内侧）17910#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1306（管箱）179Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1306（管束内侧）17910#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1315AB（壳体）Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1315AB（管束外侧）10#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1307（壳体）Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1307（管束外侧）10#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1308ABQ245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1309（壳体）Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1309（管束外侧）10#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险E1314（壳体）Q345R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险E1314（管束外侧）10#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1A低风险CCHL01G5-08轻污油自分馏来→V1309→P1212→轻污油出装置；轻污油自吸收稳定来→V130920#2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险V1309（封头）Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险V1309（筒体）Q245R2-湿硫化氢腐蚀开裂pH值、H2S分压、温度、硬度、钢材纯净度、氰化物低1C中风险表3-6公用工程工段腐蚀风险研究表回路编号回路起止点/设备编号(部位）温度（℃）压力（MPa）腐蚀介质含量材质