1145合金铝箔英文版企业标准.doc

technical data sheet aluminium foil version: 2005-12-09 supplier: alcoa shanghai aluminium product 855 jiang chuan road, minghang district shanghai 200245 china tel: 86 21 6430 1730 material: aluminum foil, including light gauge (6.30-6.5, 7, 8-9 microns) and 12-16 micra for converter foil purpose, adequate for lamination, printing, lacquering as well as 20，25，30，40 micra for pharmaceutical. 1 specifications aluminium 6.30-6.50 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145 - temper soft (o) as ordered: soft(o) other tempers on request. gaugemicrons6.30-6.50 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) acvalid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 246 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.300. selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 50 elongation%(min) 1.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. coil eccentricity mm width - 1290 o.d. 60057 * u. o. m unit of measure. 2 specifications aluminium 7 microns. foil remark property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145- temper soft (o) as ordered: soft(o) other tempers on request gaugemicrons7.0 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or bright side wound to out side.one side bright, one side dull, up to 40m wettability grade (minimum) acvalid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max. splices per reel. # 246 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.200 selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 50 elongation%(min) 1.0 outside diameter mm(max) for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. eccentricitymm width - 1290 o.d. 60057 u. o. m unit of measure 3 specifications aluminium 8-9 microns. foil remark property u.o.m *aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145- temper o as ordered: soft (o). other tempers on request gaugemicrons8-9 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dull depending on order, dull or bright side wound to out side.one side bright, one side dull, up to 40m wettability grade (minimum) acvalid for temper o (soft). . splices number (maximun) reel diameter mm 400600800 max splices per reel # 246 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.100 selected area for counting pinholes must be representative of the entire surface. tensile strength mpa50 elongation%(min)1.0 outside diameter mm(max) for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. eccentricitymm width - 1290 o.d. 60057 * u. o. m unit of measure 4 specifications aluminium 12-16 microns. foil remark property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145- temper soft (o) as ordered: soft (o). other tempers on request. gaugemicrons12-16 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, dull or bright side wound to out side.one side bright, one side dull, up to 40m wettability grade (minimum) acvalid for temper o (soft). . splices number (maximun) reel diameter mm 400600800 max. splices per reel #235 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.20 selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 50 elongation%(min)1.0 outside diameter mm(max) for cores of 3” i.d.(76.2mm) ,min.300 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 800 mm. widthmm 2501340 tolerance 1 ( up to 1620 mm on customer demand) measurement at 20-25 degrees. trace elements %pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. eccentricitymm width - 1290 o.d. 60057 * u. o. m unit of measure 5 specifications aluminium 20 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145/8011- temper h18 as ordered: soft(o) other tempers on request. gaugemicrons20 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) - valid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 234 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 max.3. selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 1145:160; 8011:170 elongation%(min) 1145:0.5; 80111.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 2501450 tolerance 1 width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. 6 specifications aluminium 25 microns foil remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 1145/8011- temper h18 as ordered: soft(o) other tempers on request. gaugemicrons25 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) - valid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 123 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 no pinholes selected area for counting pinholes must be representative of the entire surface. tensile strength mpa 1145:160; 8011:170 elongation%(min) 1145:0.5; 80111.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 2501450 tolerance 1 width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. specifications aluminium 30 microns foil 7 remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 8011- temper o as ordered: soft(o) other tempers on request. gaugemicrons30 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) a valid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 012 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 no pinholes selected area for counting pinholes must be representative of the entire surface. tensile strength mpa60 elongation%(min)2.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 2501450 tolerance 1 width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. specifications aluminium 40 microns foil 8 remarks property u.o.m * aluminum foil, for converter foil purpose, adequate for lamination lacquering, printing as well as household use. alloy 8011- temper o as ordered: soft(o) other tempers on request. gaugemicrons40 tolerancemicrons 8% on spot measurement. 4% on average for lots bigger than 10 tons this refers to tolerances around the technical target as set on the mill when rolling. the weighing of sample of known area will be the referred method. surface finish bright/dulldepending on order, matt or dull side wound to outside.one side bright, one side dull, up to 40m wettability grade (minimum) a valid for temper o (soft). splices number (maximun) reel diameter mm 400600800 max splice per reel. # 012 ultrasonic welding. position: longitudinal to spool axial. overlapping 5 mm. marked at the reel end by aluminum flags (10 x 10 mm) each side. pinholesnumber/sq.m pinholes/m2 according to en-546-4 no pinholes selected area for counting pinholes must be representative of the entire surface. tensile strength mpa60 elongation%(min)2.0 outside diameter mm for cores of 3” i.d.(76.2mm) ,min.350 mm and max 600mm. for cores of 150152.4 mm i.d., min. 400 mm and max. 760 mm widthmm 8001450 tolerance 1 width measurement at 20-25 degrees. trace elements % pb0.01 cd0.01 as0.01 the level of the sum of cadmium, lead, mercury and hexavalent chromium is below 100 ppm. core aluminum / steel standard core extension is 5 mm for each side with no slot on it. core i.d.mm76.20.2(aluminum) / 1510.3(steel)6” cores on demand. unwinding properties max (m)1.5 m method for testing stickiness as attached . length of foil is necessary to cause unwind max. 1.5 m on the entire length of the coil. reel lengthm +0 / -5% of the specified length for 90% of the coils. for the remaining 10%, +0 / -20%. * u. o. m unit of measure. quality record specifications 9 each shipment for each shipment alcoa shanghai shall send separately a quality record with the following information: -.company name - order number - customer order number - customer material number - date of shipment - ordered thickness - ordered width each reel for each reel listed in the record: - reel id number - net weight - thickness- alloy - width disposition of defective foil - incoming shipments are to be examined before unloading. when damaged rolls are discovered, if carrier is responsible, notation is made on freight bill before material is removed, and signed by driver and receiver. if rolls are intact and show no sign of rough handling by carrier, but still appear to have damage, the condition should be reported immediately to the shipping plant for disposition; - rejected metal, when returned, must have the foil roll identification ticket attached; - when possible, samples showing the problem should be attached to the roll and forwarded to supplier; - detection and complaint shall be made to the producing plant within 90 days of receipt of foil, except in the case of corrosion when the time limit is 60 days; - supplier has the right to make an inspection of the rejected foil prior to authorizing a return. packing specifications quantities - as specified on the purchase order with a tolerance of 10% unless otherwise stated on the order. packaging - foil rolls are to be suspended in steel racks or in wooden boxes and shall be packed in such a manner that normal handling by common carrier will ensure safe transportation without damage to foil. this includes wrapping to protect foil from water stain and corrosion identification - each rack or box in a shipment shall have its own unique identification number clearly visible from both ends of rack or box. further, each rack or box and each individual roll shall be identified with the followin