圆坯表面裂纹控制.doc

圆坯表面裂纹控制焦雪城 郑锦峰（承德市 承德建龙 邮编：067201）摘要：承德建龙圆坯连铸从4月底表面裂纹呈上升趋势，低倍表面裂纹率从3月份的0.1%上升到5月中旬的14%，严重影响到圆坯的表面质量和公司的美誉度。为了提升圆坯的表面质量和公司的美誉度从钢水质量和铸坯表面冷却入手，寻到到导致表面裂纹的真正的原因从而降低圆坯低倍的表面裂纹率。关键词：圆坯；表面裂纹；水质 Round billet surface crack controlJiao xuecheng Zheng jingfeng（Chengde City, Chengde Jianlong Postal Code : 067201）Summary：Chengde Jianlong round billet continuous casting an upward trend from the end of April, the surface crack , the low surface cracks rate rose from 0.1% in March to 14 % in mid - May , which seriously affected the round billet surface quality and the company s reputation , steel quality and the surface of the slab cooling in order to enhance the round billet surface quality and the companys reputation from the start, find a real reason to cause surface cracks the surface cracks rate thereby reducing the low round billet。Keyword：Round billet；Surface cracks；Water quality序言2011年2月份承德建龙圆坯投产，2、3月份圆坯表面裂纹率维持在0.1%以下，但是从4月份开始表面裂纹成逐渐上升趋势，不仅影响圆坯的表面质量而且影响公司的美誉度，为了提升圆坯的表面质量和公司的美誉度针对此问题展开分析。圆坯连铸从4月底表面裂纹呈上升趋势，低倍表面裂纹率从3月份的0.1%上升到5月中旬的14%。1 连铸二冷水质1.1连铸二冷水持续总硬度持续升高，加剧了喷嘴堵塞的现象发生。由于水垢导热能力差至使表面冷却不均匀产生表面细小裂纹。2011年2月份圆坯连铸投产之后连铸二冷水总硬度与表面裂纹数据如下表：月份总硬度(控制指标500mgl)低倍表面裂纹率平均值最大值最小值2月411.3442384.60%3月412.5490.43750.10%4月501.9548451.90.50%5月1日-5月21日534.8696.1403.86.90%5月12日-5月21日619.8568.8696.114.00% 从上表可以看出随着连铸二冷水总硬度的升高，表面裂纹率程很大的上升趋势。1.2 5月19日圆坯换断面时，结晶器组辊的照片如下图：从上图可以看出结晶器组辊处水垢较多，这样影响热量的传递，容易导致表面裂纹的产生。1.3 5月19日圆坯换断面时，水嘴的照片如下图：从上图可以看出水嘴表面发白，为水垢。从上述三点可以得出导致目前圆坯连铸的表面裂纹率持续上升的主要原因是连铸二冷水总硬度持续超标。2 结晶器水质2.1 5月15日圆坯结晶器下线铜管外壁如下图：5月20日下线的结晶器铜管外壁如下图：从上图可以看到结晶器铜管外壁有一层水垢。有理论计算0.1mm的水垢影响铜管15%的热量传递，热量传递不均匀是导致裂纹产生的原因之一。2.2 5月20日下线结晶器下法兰处的物质如下图从上图可以看出结晶器水质较差，导热不均匀容易引起表面裂纹产生。2.3 5月20日下线结晶器水锋处的物质如下图从上图可以看出结晶器水中悬浮物较多，影响结晶器的冷却效果。容易导致裂纹产生。综上所述可以看出结晶器水质差也是导致目前圆坯连铸的表面裂纹率