南玻低铁超白玻璃性能.doc

Low Iron Solar GlassCSG low iron solar glass, designed and developed independently by CSG, is the new generation of glass for solar modules and CSG reserves the products Intellectual Property Rights. The glass observes the properties of high solar transmittance, superior physical strength and significant flatness. Besides, with other performances and specifications equal to or better than those of similar products on global market, the products will adequately meet the solar industries booming demands on high quality low iron glass. Therefore, the solar modules manufacturers competitive ability will tremendously hike in solar energy markets.Parameter 1. Thickness：2.5mm10mm；Standard thickness 3.2mm and 4.0mm 2.Thickness Tolerance: 3.2mm0.20mm；4.0mm0.30mm; tolerance for other thickness should be confirmed by the seller and buyer 3.Max size：2250mm3300mm 4.Solar Transmittance (3.2mm):91.6% 5.Iron Content：120ppm Fe2O3 6.Poissons Ratio：0.2 7.Density：2.5 g/cc 8.Youngs Modulus：73 GPa 9.Tensile Strength：42 MPa 10.Hemispherical Emissivity：0.84 11.Expansion Coefficient：9.03x10-6/ 12.Softening Point：720 13.Annealing Point：550 14.Strain Point：500 CSG low iron solar glass is the ideal encapsulation material for solar thermal and photovoltaic modules. To meet customers diverse requirements, we are producing 3 series of low iron solar glass:1.Primary2.Tempered3.Anti-reflective CoatingPrimaryThickness: 2.5mm-10mm；Standard 3.2mmMax sizes：2250mm3300mmSolar Transmittance（3.2mm）：91.6%Quality Standard：CSG Solar Grade Primary StandardTemperedThickness：2.5mm-10mm； Tempered glass：Tempered Min 2.8mmMax size (3.2mm): 1000mm2000mmQuality Standard: GB15763.2-2005，AS/NZS 2208：1996，EN12150/DIN1249D，ASTM-E-903（891）-96, JISAnti-reflective CoatingLow-iron solar glass, combined with nanometer anti-reflective coating technology, is applied for solar modules. It increases solar transmittance by way of decreasing light reflectance, thus increasing the solar cell efficiency. Besides, it reduces the reflected glare of the glass and the pollution caused by the reflectance to the environment. The super water-wet behavior of the coating could in some degree protect the dust and dirt from shading the light and improve the self-cleaning of the glass so that the solar cell could maintain high efficiency. Light Transmittance：Increase by above 2%（400-1100nm）Module Output：Increase by above 2%Thickness：2.5mm-10mm；Tempered Min 2.8mm;Maximum size（Thickness 3.2mm）：1000mm2000mmSolar Transmittanc