钢管在不同温度下的许用应力

常用钢的化学成分和力学性能01.碳钢板(a) Q235-A.F钢表1-10钢的化学成分化学成分%cSiMnps0.14至0.22 0.070.30至0.600.0450.050表1-11钢板的力学性能和冷弯性能板厚度(mm)0g b(Mpa)抗拉强度10g s(Mpa)屈服点s(%)冷弯试验1802-3375-50023520D=1.5a3-3.5213.5-4224-16375-50023525D=1.5a表1-12钢板的许用应力板厚度(mm)下一温度(c)下的许用应力(Mpa)201001502002503-4113113113105944.5-1611311311310594(b) Q235-钢板表1-13钢的化学成分化学成分(%)cSiMnps0.14至0.220.12-0.300.30至0.650.0450.050表1-14钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)冷弯试验1802-3375-50023520D=1.5a3-3.5213.5-4224-16375-5023525D=1.5a16-40375-5022524D=1.5a表1-15钢板的许用应力板厚度(mm)下一温度(c)下的许用应力(Mpa)201001502002503003503-41131131131139494864.5-1611311311311394948616-40113113113107919183(c) Q235-B钢板表1-16钢的化学成分化学成分%cSiMnps0.220.12-0.300.700.0450.045表1-17钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)Akv(垂直)(j)冷弯试验1802-3375-50023520-D=1.5a3-3.5213.5-4224-16375-502352527D=1.5a16-40375-502252427D=1.5a表1-18钢板的许用应力板厚度(mm)下一温度(c)下的许用应力(Mpa)201001502002503003503-41131131131059486774.5-1611311311310594867716-4011311310799918375(d) Q235-C钢板表1-19钢的化学成分化学成分%cSiMnps0.180.12-0.300.35-0.800.0400.040表1-20钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)0Akv(垂直)(j)冷弯试验1802-3375-50023520-D=1.5a3-3.5213.5-4224-16375-502352527D=1.5a16-40375-502252427D=1.5a表1-21钢板的许用应力板厚度(mm)下一温度(c)下的许用应力(Mpa)201001502002503003504003-41251251251161049586794.5-1612512512511610495867916-40125125119110101928377(e) 20HP钢板表1-22钢的化学成分化学成分%cSiMnps0.220.350.35-0.65 0.035 0.035表1-23钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)Akv(水平)(j)冷弯试验1802.5-1.23902452527D=1.5a(6) 15MnHP钢板表1-24钢的化学成分化学成分%cSiMnps0.12至0.200.350.65-1.00 0.035 0.035表1-25钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)Akv(水平)(j)冷弯试验180 o2.5-1.24402952627D=2a(7) 20R钢板表1-26钢的化学成分化学成分%cSiMnps0.200.15-0.300.40至0.90 0.035 0.030表1-27钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)0Akv(垂直)(j)冷弯试验1806-16400-5202452531D=2a16-3623536-6022560-100390-51020524表1-28钢板的高温屈服强度板厚度(mm)以下温度(c)下的屈服强度(Mpa)不等于20025030035040045021-3618616715313912912136-6017816114713312311660-100164147135123113106表1-29钢板的许用应力板厚度(mm)下一温度(c)下的许用应力(Mpa)201001502002503003504004254504756-16133133132123110101928683614116-3613313212611610495867978614136-6013312611911010192837775614160-1001281151101039284777168614102.低合金高强度钢板(a) 16MnR钢板表2-9钢的化学成分化学成分%cSiMnps0.200.20至0.551.20-1.60 0.035 0.030表2 10钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)Akv(水平)(j)冷弯试验1806-16510-6403452131D=2a16-36490-62032521D=3a36-60470-6003052160-100460-59028520100-120450-58027520表2 11钢板的高温屈服强度板厚度(mm)以下温度(c)下的屈服强度(Mpa)不等于20025030035040045021-3625523521520019018036-6024022020018517516560-100225205185175165155100-120220200180170160150表2-12钢板的许用应力板厚度(mm)下一温度(c)下的许用应力(Mpa)201001502002503003504004254504756-1617017017017015614413412593664316-3616316316315914713412511993664336-6015715715715013812511610993664360-100153153150141128116109103936643100-12015015014713812511310610093664315MnVR表2-13钢的化学成分化学成分%cSiMnpsv0.180.20至0.551.20-1.60 0.035 0.0300.04-0.12表2 14钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)Akv(水平)(j)冷弯试验1806-16530-6653901931D=3a16-36510-6453701936-60490-62535019表2 15钢板的高温屈服强度板厚度(mm)以下温度(c)下的屈服强度(Mpa)不等于20025030035040045021-3629528026024022020536-60280265245225210195表2-16钢板的许用应力板厚度(mm)下一温度(c)下的许用应力(Mpa)201001502002503003504006-1617717717717717717215914716-3617017017017017016315013836-60163163163163163153141131(c) 15MnVNR钢板表2-17钢的化学成分化学成分%cSiMnpsvn0.200.20至0.551.30-1.70 0.035 0.0300.10至0.200.010至0.020表2 18钢板的力学性能和冷弯性能板厚度(mm)10g b(Mpa)10g s(Mpa)s(%)Akv(水平)(j)冷弯试验1806-16570-7104401834D=3a16-36550-6904201836-60530-67040018表2 19钢板的高温屈服强度板厚度(mm)