过热器作业指导书编号24

过热器焊接作业指导书1、项目工程概况及工程量11项目工程概况过热器系统主要由前顶棚过热器、后烟道包墙过热器、低温过热器、屏式过热器、末级过热器及屏式过热器间隔管组成。具体流程蒸汽从启动分离器经导气管进入顶棚过热器进口集箱经炉膛及水平烟道顶棚管进入烟道入口前墙上集箱，烟道前墙上集箱再分出两路，一路由后烟道前墙过热器到尾部环形集箱；一路经后顶棚过热器到后烟道后墙再到尾部环形集箱，这两路通过尾部环形集箱后，经烟道侧墙再到后烟道出口集箱，由导气管导入到中间隔墙进口集箱经中间隔墙到中间隔墙下集箱，进入低温过热器，再由低温过热器管排到低温过热器出口集箱，经过导气管到屏式过热器入口汇集集箱经过屏式过热器到屏式过热器出口汇集集箱，经过导气管到末级过热器入口汇集集箱经过末级过热器到末级过热器出口汇集集箱后成为主蒸汽。12主要工程量（每台炉）过热器焊口量如下表所示名称材质规格数量焊接方法焊接材料炉膛及水平烟道顶棚管15CRMOG6359384WS/DSR307/TIGR30炉膛及水平烟道顶棚管SA213T1215CRMOG6359384WS/DSR307/TIGR30后烟道顶棚管SA213T1215CRMOG44563192WS/DSR307/TIGR3015CRMOG5781193WS/DSR307/TIGR30SA213T1215CRMOG5781384WS/DSR307/TIGR30后烟道前包墙15CRMOG445634WS/DSR307/TIGR3015CRMOG44563384WS/DSR307/TIGR30后烟道后包墙SA213T1215CRMOG44563192WS/DSR307/TIGR30SA213T1215CRMOG6359238WS/DSR307/TIGR30后烟道左侧墙15CRMO6359119WS/DSR307/TIGR30SA213T1215CRMOG6359238WS/DSR307/TIGR30后烟道右侧墙15CRMO6359119WS/DSR307/TIGR30SA213T1215CRMOG6359382WS/DSR307/TIGR30后烟道中间隔墙15CRMO6359191WS/DSR307/TIGR30低温过热器12CR1MOVG5194760WSTIGR3112CR1MOVG5187760WSTIGR3115CRMO12CR1MOV5187760WSTIGR3015CRMOG5785760WSTIGR3015CRMOG578760WSTIGR30SA213T1215CRMOG578380WSTIGR30SA213T2238561680WSTIGR40屏式过热器SA213T9138661680WSER90SB9SA213T2238564WSTIGR40SA213T9138566WSER90SB9SA213TP347H386616WSH1CR19NI9NB屏式过热器间隔管SA213T9138664WSER90SB9SA213T914458600WSER90SB9末级过热器SA213T9144575600WSER90SB9一过出口至屏过入口连接管SA335P1212CR1MOVG508802WS/DSR307/TIGR30一过出口至屏过入口连接管SA335P125088010WS/DSR307/TIGR30屏过出口至末过入口连接管SA335P91508708WS/DSER90SB9/E9015B9屏过入口汇集集箱至屏过入口集箱连接管SA335P121683030WS/DSR307/TIGR30屏过入口汇集集箱至屏过入口集箱连接管SA335P12SA336F121683030WS/DSR307/TIGR30屏过出口集箱至屏过出口汇集集箱连接管SA335P911683030WS/DSER90SB9/E9015B9屏过出口集箱至屏过出口汇集集箱连接管SA335P91SA336F911683030WS/DSER90SB9/E9015B9末过入口汇集集箱至末过入口集箱连接管SA335P911682530WS/DSER90SB9/E9015B9末过入口汇集集箱至末过入口集箱连接管SA335P91SA336F911682530WS/DSER90SB9/E9015B9末过出口集箱至末过出口汇集集箱连接管SA335P912194030WS/DSER90SB9/E9015B9末过出口集箱至末过出口汇集集箱连接管SA335P91SA336F912194030WS/DSER90SB9/E9015B9主蒸汽管道SA335P915088012WS/DSER90SB9/E9015B9一级过热器出口集箱12CR1MOVG508951WS/DSR317/TIGR31末级过热器入口汇集集箱SA335P91508701WS/DSER90SB9/E9015B9末级过热器出口汇集集箱SA335P915081001WS/DSER90SB9/E9015B9后烟道中间隔墙入口集箱SA335P12273651WS/DSR307/TIGR30后烟道中间隔墙下集箱SA335P12273671WS/DSR307/TIGR30后烟道下部环形集箱SA335P12457986WS/DSR307/TIGR30包墙连接管SA335P122193558WS/DSR307/TIGR30顶棚入口集箱连接管SA335P122193524WS/DSR307/TIGR302项目作业进度的安排21过热器地面组合从4月中旬开始，施工工期为2个月，到6月中旬结束。过热器系统安装从6月上旬开始，施工工期为4个月，到10月上旬结束。3作业准备工作及条件31作业人员的质量311劳动力计划合金钢小口径管焊工20人合金钢大口径管焊工10人技术员1人班长1人质检员1人312施焊人员必须经DL/T6791999焊工技术考核规程考试合格，有相应项目合格证，且在有效期内。313焊工要有高度的责任感及良好的工作作风，且要有熟练的操作技能。314施焊人员要熟悉作业指导书，了解施焊要求，凡有与作业指导书不符之处拒绝施焊。315焊接技术员在开工前要及时交底，使焊工了解焊接方法及工艺要求，且要及时解决现场发生的技术问题。316焊接质检员要持证上岗，要经常深入施工现场，严把质量关，督促焊工做好自检工作及自身的二级检查工作。317焊接检验及热处理人员要有相应专业的有效合格证书，才能进行相应的焊接检验及热处理工作。32作业机械、工具、仪器、仪表的要求321工机具计划序号名称型号规格单位数量1逆变焊机ZX7400GST台202氩弧焊枪把303焊条保温桶W3（PR4）只204电焊钳300A把405面罩把506氩气流量计只307去渣锤把208锋钢凿子把209电焊皮线25MM2米150010半圆锉8把20所有仪表必须经过校验，合格后方可使用。322电焊机要性能良好、运转正常，电焊机的电流表、电压表要检验合格，接地装置良好。323电焊机要集中布置，焊机的二次线要连接牢固，统一布置，走线规范。324氩气表检验合格，氩弧焊把及氩气带无泄露，氩气带内部要保持干燥不能受潮。氩弧焊枪导电端接触良好，氩气压力正常，气流畅通。325电焊带应无裸漏之处，如有损坏要用黑胶布包好或更换新的。326电焊机要有防护棚，保证其工作环境良好，保证焊接工作正常进行。327电焊把钳随焊工习惯选用。33作业环境的要求331焊接允许的最低环境温度如下A类SA106C、SA210C、碳素钢为10。A、A、B类（12CR1MOV、15CRMO低合金钢、普通低合金钢）为0。B、B类（1CR18NI9TI、1CR20NI14SI2中、高合金钢）为5。C类钢不作规定332焊接施工场所应搭设防护棚，做到防风、防雨、防潮、防寒，以免影响焊接质量。333焊接场所应保证焊工有足够的施焊空间，不能影响焊工正常施焊。334焊接场所周围5米内不允许有易燃易爆物品，如汽油、乙炔等。34焊接材料的选用和使用341纯度9995以上的瓶装氩气。342钨极氩弧焊用的电极宜采用铈钨棒，规格25MM。343按照图纸核对被焊母材材质，正确选用焊接材料如下表所示序号母材材质焊丝焊条115CRMOGTIGR30R3072SA213T1215CRMOGTIGR30R307312CR1MOVGTIGR31R317415CRMO12CR1MOVTIGR30R3075SA213T22TIGR406SA213T91ER90SB9E9015B97SA213TP347HH1CR19NI9NB8SA335P1212CR1MOVGTIGR30R3079SA335P12TIGR30R30710SA335P91ER90SB9E9015B911SA335P12SA336F12TIGR30R30712SA335P91SA336F91ER90SB9E9015B9344焊丝使用前应清除锈垢和油污，至露出金属光泽。345焊条使用前应按说明书要求进行烘干，重复烘干不得超过两次，使用时应装入温度保持在100150的专用保温箱（筒）内，随用随取。346存放一年以上的焊条用于重要部件焊接时，如对其质量发生怀疑，应重新做出鉴定，符合要求后方准使用。347合金焊条、焊丝在使用应进行光谱复检。348使用的焊接材料应有制造厂的质量合格证。凡无质量合格证或对其质量有怀疑时，应按批号抽查试验，合格者方可使用。349焊前领用的焊条，应计划当天的用量，使用的时间及部位应登记。35坡口的清理及准备351管子坡口外部距被焊端1015MM以内应清理干净，去除油、锈、漆、垢等，内壁距焊端10MM范围内同样清理。352管口两端若内径不等应进行修磨，修磨时内坡口应平缓，角度不大于15度。353坡口有影响焊接质量缺陷时应修复或补焊至符合要求。354坡口型式应符合图纸及相关规程的要求。355对口时应做到内壁齐平，外壁错口值在允许范围，管子对口弯折度不超标。356对口时应保证间隙在允许范围内，焊口局部间隙过大时，应设法修整到规定尺寸，严禁在间隙内加填塞物。357对口完成后要加以固定不能在施焊时有移动，以防止在焊接和热处理过程中产生变形和附加应力。358除设计规定的冷拉口外，其余焊口严禁强力对口，更不允许利用热膨胀法对口，以防止引起附加应力。359根据焊接的相互位置，合理选择焊接顺序，一般成片管排应先焊间细小的焊口。4作业程序及作业方法41壁厚6MM的焊口，采用全氩弧焊接，壁厚6MM的焊口采用氩弧打底电焊盖面的焊接方法。42焊接施工要执行图纸要求。43氩弧焊时采用直流正接法，既焊件接正极，电焊盖面时采用反接。44引弧方法为接触引弧，且要求在坡口内引弧，引燃后应保证起弧点熔透，严禁在被焊件表面引燃电弧，试验电流，或随意焊接临时支撑物。45手工钨极氩弧焊接操作技术。451管子焊接时，其焊接方向不限，一般采用左向焊法，即延焊接方向，焊丝在前焊枪在后。为了送丝方变，不影响焊工视线和防止喷嘴被烧损，钨极应伸出喷嘴端面约69MM，钨极端部与熔池表面的距离，即电弧长度应保持24MM。电弧过短，钨极易与焊丝和熔池相碰，造成焊缝表面和夹钨缺陷，并破坏电弧的稳定燃烧；电弧过长，则引起电弧飘浮，易产生未焊透缺陷。为了加强氩气保护效果，喷嘴与焊件应尽量垂直或保持较大的夹角，一般为7085而焊丝和焊件的夹角则较小，一般为1520。452起弧。焊接开始时，先用电弧将母材加热，待形成熔池后，立即填加焊丝。为了防止起弧处产生裂纹，始焊速度应适当简慢，并多填些焊丝，使焊缝加厚，在两侧坡口间搭成焊桥，以桥为基础进行焊接。453收弧。中间收弧时，先将熔池填满，把电弧拉向坡口的一侧甩弧熄灭。最后收尾时将始焊侧的焊道端头熔化，将已熔金属与新熔化的熔池相碰接，再将新出现的熔池填满连接在一起，然后按动电流衰减按钮，使焊接电流逐渐减小，最后将电流熄灭，然后关闭氩气。454接头。焊接时需要变换握丝位置时，先将焊丝末端和熔池相接触，同时将电弧稍作后移，或引向坡口一边，待熔池凝固与焊丝末端粘在一起的刹那间，迅速变换握丝位置，完成这一动作后将电弧立即恢复原位继续焊接，焊接过程中尽量避免熄弧，以减少冷接头。455送丝动作。以左手拇指、食指、中指握焊丝，焊丝末端应始终处于氩气保护区内。填丝动作要轻，不得扰动氩气保护层，以防空气侵入。采用外填丝法，焊接时可用连续送丝或间断送丝法，间隙较大和焊接次层的情况下焊丝应跟焊枪作横向同步摆动，任何情况下焊丝熔端都不能离开氩气保护区，以免高温氧化影响焊接质量。456氩弧焊焊接工艺参数选择如下表所示序号材质规格MM焊丝直径（MM）氩气流量L/MI电流范围A电压范围V焊接速度MM/MIN115CRMOG6359257990110101250602SA213T1215CRMOG6359257990110101250603SA213T1215CRMOG4456325799011010125060415CRMOG5781257990110101250605SA213T1215CRMOG578125799011010125060615CRMOG4456325799011010125060712CR1MOVG5194257109010510155060812CR1MOVG5187257109010510155060915CRMO12CR1MOV51872571080100101545551015CRMOG5785257990110101250601115CRMOG5782579901101012506012SA213T1215CRMOG5782579901101012506013SA213T223856258101051261015455514SA213T91386624810851101015304515SA213T91385624810851101015304516SA213TP347H38662571070901015457017SA213T91445824810851101015304518SA213T914457248108511010153045519SA335P1212CR1MOVG5088025791101301012405020SA335P12508802579901101012506021SA335P9150870258101001201015455522SA335P12168302579901101012506023SA335P12SA336F12168302579901101012506024SA335P9116830258101001201015455525SA335P91SA336F9116830258101001201015455526SA335P9116825258101001201015455527SA335P91SA336F9116825258101001201015455528SA335P9121940258101001201015455529SA335P91SA336F9121940258101001201015455530SA335P915088025810100120101545553112CR1MOVG5089525791101301012405032SA335P9150870258101001201015455533SA335P91508100258101001201015455534SA335P12273652579901101012506035SA335P12273672579901101012506036SA335P12457982579901101012506037SA335P122193525799011010125060457对口点固焊4571点固焊均采用钨极氩弧焊。4572管排吊焊在平焊部位点固一点或对称点固两处，每排焊口应从两端先点固，然后依据间隙最小的先点固，点固焊口至少为每排管的80后才能进行氩弧打底焊接。4573大径管吊焊口在两侧立焊及平焊位置各点固一点。4574点固焊缝长度为1520MM，点固焊缝厚度不小于3MM且不大于4MM。4575点固焊两端应修磨成缓坡，以利于打底施焊时连接。点固焊后应认真检查，没有缺陷后方可进行氩弧打底焊。458氩弧打底焊的焊层厚度不大于3MM，打底层焊缝检查合格后应急时进行次层焊缝的焊接，次层氩弧焊或电弧焊均应用尽量减小电流，防止产生缺陷或击穿打底层焊缝。459全氩弧焊要求两遍成型，不论全氩弧或氩弧打底电焊盖面的管排焊接，为减少焊接变形和防止冷接头产生缺陷，可以采用两人对称焊的焊接方法。4510坡口内或管子上对口用固定块，打底焊接完成后要磨光焊点与母材一样。46手工电弧焊接的操作技术。461焊接时使用连弧焊法，这种焊法熔池温度是靠调节电流大小控制的。施焊中，随着时间和焊缝的延伸，母材温度逐渐升高，在维持电弧稳定燃烧和不断弧的条件下，可随时改变电流的大小，保持熔池有一定的温度和几何尺寸。4611焊条的倾角。A）水平及斜位固定管施焊中焊条应随管子弧光变化调整焊条倾角一般应保持在7080之间，焊条端部应始终指向对口间隙中心，并与管面保持垂直。一般在下爬坡焊口中心另一面1020MM处开始引弧，焊至仰焊部位时按正常倾角施焊，焊至上爬坡时，将焊条转一个方向，焊条向未焊部位倾斜，以保正接头熔化良好和平焊位置焊透。B）垂直固定管，焊条与管子在两个方向上均有倾角，一个是与对口方向下垂1030，另一是向为焊侧方向倾斜7080，并维持始终。4612焊条的摆动方法。A）水平固定管焊接时采用连弧焊接法，用反月牙形、正月牙形或小折线形法施焊，焊接时均应在一侧稍作停顿将电弧再移向另一侧稍作停顿再移回原侧的续焊处，以此类推进行焊接。两端停顿的主要目的是保证焊缝与母材熔化良好，避免出现夹渣、未熔合缺陷。焊条移动时不宜过快，以防铁水不连贯，出现漏焊或中间形成凹陷。A）直固定管焊接时采用连弧分层分道焊法，焊缝盖面时的焊道分托底焊道、中间焊道、补充焊道三道。每道焊条摆动方法是不一样的，托底焊道一般采用小斜划圈法；中间焊道采用大斜锯齿形或大斜划圈形，靠近上坡口时稍作停顿，保证上面焊缝填满，不致形成滑坡形焊道；补充焊道采用快速推拉法或小斜锯齿形焊法，是为了避免焊缝与母材熔合处出现咬边或未熔合缺陷，并保证焊缝的压边量。C）斜位固定管焊法与水平固定管相近，施焊时焊条仍须做横向摆动，但注意的是必须形成与地面水平的熔池。难点是上下两个接头处，操作不当焊缝不美观且容易造成焊缝外表缺陷。一般用推手法，焊接时由仰焊下部开始引弧，向两侧横拉，初时焊缝宽度较窄，逐渐加到正常焊缝宽度继续施焊，焊至平位时，由正常焊缝宽度逐渐变窄，形成斜坡焊缝；焊接另一侧时，亦由仰焊部位沿已焊窄焊道开始，焊条向上摆动，逐渐加宽到规定尺寸，焊至平焊位时，将原斜坡焊缝填满，形成正常宽度的焊缝。4613焊缝的起头、接头和收头A）起头焊接时电流不宜过大，要比正常焊接电流小1015，快速焊接，以免击穿氩弧打底层。B）接头。接头在始焊前，应将端部剔成斜滑坡形，以保证接头处良好熔合，避免接头过高和未焊透缺陷，也便于操作。引弧时由熔坑端部开始，延熔坑边缘向熔坑尾部移动，焊条左右摆动，始接头良好熔合，然后延未焊母材继续施焊。C）收头。焊接收头时，应以变阻器逐渐减小电流，用溶化金属填满熔坑，电弧向前拉出迅速熄灭电弧，以免出现缩孔。462电弧焊接工艺参数选择如下表所示序号材质规格MM焊条直径MM电流范围A电压范围V焊接速度MM/MIN25759520257585115CRMOG6359328010020255565257595202575852SA213T1215CRMOG6359328010020255565257595202575853SA213T1215CRMOG4456332801002025556525759520257585415CRMOG5781328010020255565257595202575855SA213T1215CRMOG578132801002025556525759520257585615CRMOG4456332801002025556532120140202280907SA335P1212CR1MOVG5088040160170202270140257595202575858SA335P1250880328010020255565321001252030801009SA335P915087040140174020301001502575952025758510SA335P12168303280100202555652575952025758511SA335P12SA336F12168303280100202555653210012520308010012SA335P911683040140174020301001503210012520308010013SA335P91SA336F911683040140174020301001503210012520308010014SA335P911682540140174020301001503210012520308010015SA335P91SA336F9116825401401740203010015016SA335P91219403210012520308010040140174020301001503210012520308010017SA335P91SA336F912194040140174020301001503210012520308010018SA335P915088040140170203010015032120140101240501912CR1MOVG50895401601702022701403210012520308010020SA335P91508704014017020301001503210012520308010021SA335P9150810040140174020301001502575952025758522SA335P12273653280100202555652575952025758523SA335P12273673280100202555652575952025758524SA335P12457983280100202555652575952025758525SA335P1221935328010020255565463厚壁管多层多道焊接时，要采用两人对称焊接，以减少焊接变形。当氩弧打底根层完成后，第一层填充盖面焊接时宜采用小电流快速焊，以免击穿打底层焊缝。其它层的电焊盖面所用的焊条直径不大于4MM，焊道的单层厚度不大于所用焊条直径加2MM，且不大于5MM，避免采用大电流超厚度堆焊焊缝，否则易产生过烧组织。464焊条在焊接过程中允许摆动，单焊道摆动宽度不大于所用焊条直径的5倍。465施焊过程中要特别重视焊缝的层间清理及检查工作，焊一层清理检查一层，尤其应注意接头及焊缝边缘处的清理，发现缺陷及时处理，不允许用焊接加大熔深的办法来消除缺陷。466焊层与焊道之间的接头应错开2530MM，各层焊道之间不应形成不易熔透的深沟，如发现处理后再行施焊。467最外层电焊盖面应采用32MM的焊条，这样可以保证焊缝表面没有组糙的焊道波纹，焊缝外型美观。47施焊过程除工艺和检验上要求分次焊接外，应连续完成，若被迫中断，应采取防止裂纹措施（如后热、缓冷、保温等）再焊时，应仔细检查，并确认无裂纹后，方可按工艺要求继续施焊。48焊口焊完后应进行清理，经自检合格后在焊缝附近打上焊工本人的代号钢印。49焊前预热要求491预热温度如下表所示管子规格（MM）材质预热温度（）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管子外径大于219MM或壁厚大于等于20MM时，采用电加热进行预热。493壁厚大于或等于6MM的合金钢管子或管件，在负温度下焊接时，预热温度应比下限高2050。壁厚小于6MM的低合金钢管子及壁厚大于15MM的碳素钢管子，在负温度下焊接时，也应适当预热494预热宽度从对口中心开始，每侧不少于焊件厚度的三倍且不小于100MM。495施焊过程中，层间温度应不低于规定的预热温度的下限，且不高于400。496焊接工作因某种原因中断时，要有保温缓冷措施，恢复焊接工作前应先恢复预热温度。410焊后热处理4101热处理温度如下表所示管子规格（MM）材质热处理温度（）15CRMOG6359焊后缓冷SA213T1215CRMOG6359焊后缓冷SA213T1215CRMOG44563焊后缓冷15CRMOG5781焊后缓冷SA213T1215CRMOG5781焊后缓冷15CRMOG44563焊后缓冷SA213T1215CRMOG44563焊后缓冷12CR1MOVG519472075012CR1MOVG518772075015CRMO12CR1MOV5187焊后缓冷15CRMOG5785焊后缓冷15CRMOG578焊后缓冷SA213T1215CRMOG578焊后缓冷SA213T223856焊后缓冷SA213T913866750780SA213T913856750780SA213T914458750780SA213T9144575750780SA335P1212CR1MOVG50880650700SA335P1250880670700SA335P9150870750780SA335P1216830670700SA335P12SA336F1216830670700SA335P9116830750780SA335P91SA336F9116830750780SA335P9116825750780SA335P91SA336F9116825750780SA335P9121940750780SA335P91SA336F9121940750780SA335P915088075078012CR1MOVG50895720750SA335P91508100750780SA335P1227365670700SA335P1227367670700SA335P1245798670700SA335P12219356707004102热处理加热方法选用远红外线加热器进行加热。4103加热宽度从焊缝中心算起，每侧的宽度不小于壁厚的三倍。且不小于60MM。保温宽度从坡口边缘，每侧不得少于管子壁厚的5倍，且每侧应比加热器的安装宽度增加100MM,保温厚度以4060MM为宜。4104焊接热处理升、降温速度为6250/（单位为/H，其中为焊件厚度）且不大于300/H，降温时，温度在300度以下可不控制。4105热处理测温点应对称布置在焊缝中心两侧，且不少于两点，水平管段的测点应上下对称布置。4106焊接热处理恒温过程中，承压管道在加热范围内，任意两点的温差应小于50。4107所有缺陷均应在热处理前处理完，否则修复后应重做热处理。4108焊接接头热处理后，应做好记录和标记。411P91/T91钢管焊接工艺411191钢管及P91小径薄壁钢管推荐采用全氩弧焊方法P91钢大径厚壁管采用氩弧焊打底、焊条电弧焊填充及盖面的组合焊接方法。4112氩弧焊WS打底焊接41121为防止根层焊缝金属氧化，氩弧焊打底及焊条填充第一层焊道时，应在管子内壁充氩气保护（或涂“太阳”免充氩焊接保护剂）。41122太阳免充氩焊接保护剂使用方法41123清除油污“太阳”对灰尘和氧化膜有清除作用，但是油渍在涂前应当清除。41124混合“太阳”焊接保护剂在供货状态下为粉末状，使用时需要与1甲醇（或酒精）（）专用粘合剂混合。41125与甲醇（或酒精）的混合方法粉末与甲醇的重量混合比例为21，搅拌均匀后为奶油状的混合物，将混合物停留约5分钟后涂于焊口的背面，停留23分钟，就可以进行焊接。该方法主要用于被焊工件在装配或焊接过程中无严重震动的情况下。如有严重震动，则可能造成涂层的脱落。此时，需采用以下混合方法。41126与专用粘合剂混合为防止由震动造成的涂层脱落，可以将粉末和专用粘合剂按照581的比例（质量比）进行混合，然后再加入丙酮将混合物稀释成为奶油状，将混合物涂于焊口背面，宽度约3MM，厚度约1MM。停留约58分钟后，就可以进行焊接。41127焊接时机在涂于焊口背面后可以停留几分钟再进行焊接，也可以几天后再焊接，保护剂不会因为时间延长而失效。41128焊接电流可以正常的焊接电流施焊，也可以大于正常焊接电流的10的电流进行焊接。41129对口间隙一般对口间隙为25MM。4113内壁充氩施工方法41131充氩保护范围以坡口中心为准，每侧各200300MM处，以可溶纸或其它可溶材料，用耐高温胶带粘牢，做成密封气室。41132采用“气针”从坡口间隙或一端中插入进行充氩，开始时流量可为1020L/MIN，施焊过程中流量应保持在810L/MIN4114氩弧焊打底时，焊接规范参数推荐如下焊丝选用25MM，钨极为25MM，氩气流量为710L/MIN焊前预热温度为150250，焊接电弧电压为1015V，焊接电流为100120A，焊接速度为4555MM/MIN。41141氩弧打底的焊层厚度控制在2832MM范围内。41142焊条电弧焊（DS）填充、盖面焊接41143施工过程中，应注意层间温度的保持，推荐的层间温度为200300。41144为保证后一焊道对前一焊道起到回火作用，焊接时每层焊道厚度的控制约为焊条直径。41145焊条摆动的幅度，最宽不得超过焊条直径的4倍。41146焊条电弧焊各层焊道的主要工艺参数参考值见下表焊层数焊条直径（MM）焊道数焊接电流A电弧电压V焊接速度（MM/MIN）每层填充金属厚度（MM）2332110012520308010030454021401702030100150356144021501702030100150401540315017020301001503516323100125203080100205作业的质量要求及施工验收标准/规范51质量要求511焊接接头表面质量应符合下表（一）要求表（一）焊缝余高MM焊缝宽窄差MM弯折MM接头类别焊缝成型10101010D100D100外壁错口MM咬边MM裂纹、弧坑、气孔、夹渣优良焊缝过渡圆滑，匀直，接头良好02025231/1003/20001且1无无合格焊缝过渡圆滑，接头良好025033401且4H05，I01L,且40优良焊缝过渡圆滑，匀直，接头良好02032301且1无合格焊缝过渡圆滑，接头良好0304341/1003/20001且4H05，I01L,且40无512质量验收标准执行火力发电厂焊接技术规程（DL/T8692004）及火电施工质量检验及评定标准焊接篇1996版。513焊接角度变形1/100。514外观检查不合格的焊缝不允许进行其它项目的检查。515焊缝根部凸出2MM，内凹15MM,且不大于焊缝长度的25。516合金钢件焊后应对焊缝进行光谱复查，规定如下（1）锅炉受热面管子不少于10。（2）其它管子和管件100。（3）光谱复查应根据每个焊工的当日工作量进行517焊缝无损探伤检验为100检验，受热面合金小径管射线检验比例100。结果的评定按钢制承压管道对接焊缝接头射线检验技术规程DL/T8212002和管道焊接接头超声波检验技术规程（DL/T8202002）标准进行。518点固焊与正式焊要求相同，点固焊位置应置于不影响视线便于操作处，焊点长度不超过10MM，厚度不超过3MM，点固焊后应检查焊点质量，如有缺陷应立即清除，重新进行点焊。519过热器管排焊接时，宜两人对称施焊，并且先点焊间隙小的，后点焊间隙大的。第一层打底焊顺序也是如此，待全部焊口打底焊缝完成后，再进行盖面层的焊接,氩弧焊接时，管内严禁有穿堂风。5110氩弧焊焊接电流和手工电弧焊的电流应严格按照焊接工艺评定给定的电流施焊，严格控制层间温度。5111盖面前应先检查打底焊缝的质量，如有缺陷应及时消除，盖面焊接起点与结尾和打底层的焊接起点与结尾要错开。5112施焊时应特别注意两个接头处，必须熔合良好，层与层之间的氧化物、飞溅等杂质清理干净，检查合格后方可焊接次层。5113点固焊好的焊口和打过底的焊口应及时盖面，不得拖延至次日。5114焊口焊完应将焊缝两侧熔渣、飞溅物等清理干净。5115检查焊逢表面是否有缺陷，如有表面气孔、夹渣、弧坑未填满、咬边、焊缝尺寸不符合要求等，应及时进行修整，消除缺陷后重新清理干净。52焊接质量缺陷的预防及返修措施521焊接质量缺陷的预防5211按要求做好挡风防雨措施，认真清理坡口两侧，焊条按规定烘干并用保温桶盛装，焊丝清理干净，以防产生气孔、裂纹等缺陷。5212打底焊接电流、速度适当，焊条角度要正确，焊接操作要熟练，以防产生未焊透、未熔合等缺陷。5213为防止产生咬边，WS焊时，焊枪应指向母材金属，焊丝在焊缝两侧应填满，DS焊时，应选择适当的电流。焊条角度要适当，摆动时在坡口边缘要稍慢些。522焊接质量缺陷的返修5221焊接接头内部有超标缺陷时，可采用挖补方式返修，但同一位置的挖补次数不得超过两次，并应遵守下列规定1）彻底清除缺陷，尽量有机械方法加工，当不能用机械法加工而采用火焰吹割法时，需将吹割后的坡口表面打磨出金属光泽，坡口应尽量规则，避免坡口底部有尖角，轮廓突变及毛刺等。2）补焊时所采用的焊接材料、工艺与焊接施工时基本相同，尽量采用小规范焊接。3）返修完毕，按不低于原焊缝标准对补焊进行检验，发现还有不允许缺陷时，应重新挖补返修。5222焊缝表面有超标缺陷时，可用下述方法予以修复1）焊缝余高过高，余高差超标或有焊瘤时，用机械方法去除，余高不足时应将焊缝清理干净，然后补焊。2）咬边超标时，应先清理干净焊缝后补焊，弧坑、气孔、裂纹都应清理至无缺陷处，而且不应留下尖角，然后进行补焊；3）焊缝成型不好，过渡存在突变现象，应打磨成圆滑过渡。4）凡是不能采用局部补焊法修复的缺陷可采用气割法割除，重新加工坡口对口焊接。5）电弧擦伤必须将其打磨掉，打磨后的凹坑视其具体情况予以修复。6）不得对焊接接头进行加热校正。6施工过程中安全防护和文明施工标准及措施61施工项目必须办理第二种安全施工作业票，经工程处专责工程师审查批准，由班组长技术员交底，双方签字后执行（第二种安全施工作业票有效期不得超过10天）。62高处作业以及带电作业等危险性作业项目的安全措施及施工方案，应由工程部、安监部审查，总工程师批准。63同一个施工项目的安全措施方案，在环境、设备、人员等条件变化情况下，不得重复使用，必须重新编制安全措施，重新交底、签字后执行。64进入施工现场的施焊人员，必须正确佩戴安全帽及穿戴好劳动保护用品，高处作业系好安全带，注意上方落物，也注意不要向下抛物。65施工现场要有防火、防爆、防止金属飞溅引起火灾的措施，随时清除周围易燃、易爆物到十米以外，做到文明施工。66焊工在给电源合闸时应带焊接手套，合闸时要侧身，不能面对电闸，防止产生弧光烧伤事故。67如有交叉作业应设专人监护或有防护措施，否则严禁施工，以免发生物体打击及碰撞事故。68施焊人员禁止从设备上来回横空跨越，以免摔伤。69施焊时，焊条头、和焊条不得乱仍，以确保人身安全及现场的文明施工。焊条头及未用完的焊条应急时回收。610为避免焊工和其他工作人员不受弧光伤害，焊工在施焊引弧前应观察周围环境，并事先发出信号，方可开始工作。611如在夜间工作安全照明必须充足。612使用角向及电磨时要戴好防护眼镜，以免被铁屑飞溅打伤眼睛。613施工结束时，焊工应把所用工具用工具袋装好，同时关闭焊机电源，在确认无任何危险存在后方可离开现场。施工中使用履带加热器、防风棚，应注意防止着火。614文明施工责任区划分明确，无死角，责任落实，并设有明显标记，便于检查、监督。615施工用机械、设备完好、清洁，安全操作规程齐全，操作人员持证上岗，并熟悉机构性能和工作条件。616工具间等场所内部整洁，布置整齐。617现场使用的电焊机，应用电焊机集装箱集中设置；电焊机的二次线应隐蔽集中布置，并在各平台装设电焊机二次线快速接头。热处理电源要保护可靠，接地良好，防止触电。电焊线有裸露的，一定要用黑胶布包好以免电弧打伤设备或发生触电事故。618施工现场在施工过程中出现的各种坑、沟、孔洞，施工单位应根据实际情况，设置标准的与地平行的安全沟道盖板或可靠的围栏、挡脚板或警告标志。619施工现场搭设的临时施工平台和通道，应用两块以上跳板绑扎牢固，并设栏杆。620不准随意在设备、结构件上焊接临时结构，必要时要取得主管部门的同意，并出具书面通知后实施。621施工现场消灭“七头”（铁头、木头、电缆头、电焊条头、烟头、砖头、破布头），做到工完、料净、场地清。622拉电源时，严禁将电线直接勾挂在闸刀上或直接插入插座内使用，必须用插头连接。623施工单位应经常组织施工人员进行安全文明施工学习，使每位施工人员掌握安全文明施工知识，不断地提高安全文明施工意识，做到安全生产文明施工。7危险及紧急情况时的针对性预防和应急措施71触电事故应急预案711触电发生后可能的后果,电气设备易损坏；人员易电弧灼伤、呼吸困难或停止、引发其它伤害、死亡。72触电事故预防措施721对生产现场使用的临时电源、移动式电动工具以及手持式电动工具必须安装漏电保护器，并在使用前必须做试验，保证灵敏可靠动作。722用电线路及电气设备的绝缘必须良好，布线应整齐，设备的裸露带电部分必须加防护罩。723闸刀型电源开关严禁带负荷拉闸，严禁将电线直接勾挂在闸刀上或直接插入插座内使用。724施工人员必须着专用工作服，绝缘手套、绝缘鞋。电焊机二次线不允许有裸露部分。725应急措施发生触电事故时施工人员要进行触电急救，并报告生产安全事故应急处理指挥部。73高空坠落事故应急预案A防止高处坠落事故1高空作业扎好安全带，安全带必须挂于腰部以上牢固可靠位置。2铺设好跳板，跳板要帮扎牢