防静电环氧地坪施工方案

1、欢迎下载内容仅供参考防静电环氧地坪施工Anti-static Epoxy Self-leveling system抗静电环氧自流平地面The proposal ：3mm Anti-static Epoxy Self-leveling systemSikafloor 239EDFAntistatic epoxy self-leveling system抗静电环氧自流平系统Approx.Sikafloor 239EDFAntistatic epoxy self-leveling system抗静电环氧自流平系统Approx.3mmcoatingthickness涂装厚度约 3 mmSikafloo

2、r239EDFisaseamless,self-smoothing,flooringsystembasedonadvanced solvent-freeepoxysystemandselectedgradedfillers.Thecuredfloorexhibitsexcellent electrostatically dissipative behavior. The smooth, impervious surface can be easily maintained in a hygieniccondition.Sikafloor 239EDF 是一种无接缝、自流平环氧系统，它以一种先进

3、的无溶剂环氧树脂为基料，并采用专门级配的填充料。该地面具有优异的防静电性能，其表面形成光滑的无渗透的地面，易于保持卫生状态。Performance 性能:Electrostatically dissipative (Resistance to ground 106RG109 Ohm)防静电性能(106RG109欧姆)High level of aesthetics and easy to clean 高度美观，易清洗Comfort and care 舒适，安全Smooth and seamless 光滑，无缝Structure Profile 系统结构图:防静电面层 Anti-static T

4、op-coatConductiveLayerLevelayerPrimerConcreteSystem Description 系统介绍：StepStepProduct & ConsumptionApplication Method步骤产品和用量施工方法Surface Preparation:Cleaning, grinding and shot blasting基层处理清理，研磨和喷砂处理Primer:Sikafloor161+石英砂 0.3-0.4kg/m2Trowel,roller底漆刮板，滚筒Epoxy Levelingmortar环氧找平层Sikafloor161+适量石英砂0.9k

5、g/ 0.9kg/m2Trowel刮板Conductive CopperTapeAdhibit导电铜带粘贴Conductive LayerSikafloor220W 0.1kg/m2Roller导电层滚筒Top-coatSikafloor 239EDF 1.8kg/m2Trowel刮板面层+SikaDur 505 0.6kg/m2Material Description 材料说明:Sikafloor 161 is a 2 component epoxy resin based, solvent free primer.Sikafloor 161 是一种双组分环氧树脂基无溶剂型底油Sikaflo

6、or220Wisatwopartwaterdispersed,epoxyresinwithhighconductivity是一种双组分水性环氧树脂，具有较高的导电性能。Sikafloor 239EDF is a two part, self-smoothing, coloured epoxy resin coating.Decorative and protective dissipative self-smoothing system for concrete or cement screeds with normal up to medium heavy wear.Sikafloor 23

7、9EDF 装饰和保护的涂层Sikadur 505Qisadriedfinequartzaggregate,0.1-0.3mmforfillingself-levelingfloors and as filler in Sikafloor 156/263/264 as leveling mortar or scrape layer.Sikadur 505Q是一种干燥细颗粒骨料，0.10.3 mm ，用于填充自流平地面及用作Sikafloor161/263/264自流平砂浆或刮磨层的腻子层。ThinnerDSorThinnerCisasolventforcleaningpurpose. Thinn

8、erDSor ThinnerC 是用于清洁的溶剂Application Method 施工工艺Inspection Substrate Quality 基面质量检查Theconcretesubstratemustbesoundandofsufficientcompressivestrength(minimumN/mm2)withaminimumpulloffstrengthof1.5N/mm2.混凝土基面必须密实和有足够的抗压强度（最小25 N/mm2），1.5 N/mm2。Substrateneedstobedry,moisturecontent4%.Testmethod:Sika-Tram

9、exmeteror CMmeasurement.Awaterproofinglayermustbeinstalledundertheconcreteor vapor going up will result in epoxy layer bubbling and delamination. 2 mm Sikafloor 81 EpoCem system need to be applied as a moisturebarrier.基层须干燥，含水率4%，测试方法：Sika-Tramex仪或CM测量法。混凝土基层下须设置 防水层，否则存在水汽上升导致环氧层起泡、脱落风险。建议施工2mmSika

10、lfoor81系统作为防潮层。Thesubstratemustbecleanandfreeofallcontaminantssuchasdirt,oil,grease,coatings and surface treatments,etc.基面必须清洁、无任何污染物，如：灰尘、油、油脂、涂层和表面处理等。Measure Application Conditions 施工条件测量SubstrateTemperature:+10min./+30基面温度：最低+10/最高+30Ambient Temperature +10 min. / +30 max.环境温度：最低+10/最高+30 Relati

11、veAirHumidity:80%R.H.80%相对湿度Dew Point: The substrate and uncured floor must be at least 3above dew point toreduce the risk of condensation or blooming on the floor finish.露点：基面和未固化的地面温度必须至少高于露点3，以防水汽凝结形成斑点。Substrate Preparation 基面处理re-clean the floor surface, degrease agent will be used where necess

12、ary.清洁地表，必要时使用清洁剂；Carryoutsurfacepreparationbyusingshotblastingmachine(dustfreeselfenclosedshotblastingunit)andhandtoolstoremovesurfacelaitanceandtoprovidesoundand texturedsurface.使用自动无尘喷砂设备和手动工具进行表面预处理，去除混凝土表面翻沫及松散结构，并提供涂装所需的必要的粗糙度；Removeallremainingdustanddebrisbydrybrushingandvacuumcleaning.丸及灰尘，

13、并真空吸尘；Repair all floor defects such as honey combs, scratches, working joints and so on by usingSikaDur and Sikaflex range of materials.使用SikaDur 与Sikaflex等系列产品对地面缺陷如蜂窝麻面、划痕、施工缝等进行修补；Mixing of material 材料混合:In general, all products must be mechanically mixed using an electrical power stirrer with300

14、400rpm,priortomixingstirpartAmechanically.WhenallofpartBhasbeen addedtopartA,continuouslymixfor2minutesuntilauniformmixhasbeenachieved. DependingontheproductadinthefillerorCcomponentandmixforanother2minutes until a uniform mix has beenachieved.A300 400 转速/把所有B组分加入A2 分钟直到混合均匀。根据产品加入填料或C组分， 继续搅拌两分钟直到混

15、合均匀。Toensurethoroughmixing,pourmaterialsintoanothercontainerandmixagaintoachieve a consistent mix. Over mixing must be avoided to minimize air entrapment.保证通过混合、倾倒材料进入另一容器后，再次搅拌达到一致混合。需要避免过度搅拌产生气泡Application of Sikafloor 161, consumption approx. 0.4 kg/m for primer；Application of Sikafloor 161, cons

16、umption approx. 0.4 kg/m for primer；consumption approx. 0.9 kg/m Sikafloor 161 mixed with 0.45kg/m2 quartz sand.Sikafloor 161 0.4 kg/m,2.7kg/m2Application of Conductive Copper Tape 导电铜带施工欢迎下载内容仅供参考ApplicationofApplicationofConductivelayer 导电层施工Apply with a layer of Sikafloor220W,consumptionapprox.kg

17、/m.Sikafloor 220W0.1 kg/m，Application of anti-staticTop layerApplication of anti-staticTop layer 防静电面层施工Aftercuringoftheconductivelayer,application of a layer Sikafloor with a trowel; consumption approx. 1.8kg/m Sikafloor 239EDF mixedwith0.6kg/m2 quartzsand.导电层固化后， 用刮板施工 Sikafloor7 / 8欢迎下载内容仅供参考Also apply with a spike rolling for deairing and levelling.用齿状刮刀施工并立即用带钉的滚筒排气找平。After application, clean the application tools with Thinner DS.施工结束后用