亚克力质量标准.doc

亚克力质量标准1颜色：颜色依据客户样品2表面处理： 双面蒙砂：依据客户样品；产品表面双面覆膜，膜材料以封样的样品为准3物理性能：性能Properties测试标准ASTM单位Unit3.0mm 透明SPECIFIC GRAVITY比重D7921.19Refractive Index折射率D5421.49Light Transmission透光率D1003Parallel透光率%92Total全透光%93Haze雾度%1Rupture断裂PSI11Modulus of Elasticity弹性模量PSI400Rupture断裂PSI15Modulus of Elasticity弹性模量PSI400Yield屈服PSI18Modulus of Elasticity弹性模量PSI400Shear Strength剪切强度D732PSI9Izod Notched缺口冲击强度FT.LBS0.4Charpy Unnotched无缺口冲击强度FT.LBS3.5Rockwell hardness洛氏硬度D785M95Barcol Hardness巴氏硬度D258350Thermoforming Temperature热成型温度1401802 /MIN.-264PSI热变形温度D648101Coefficient of Thermal Expansion热膨胀系数D696IN/IN- F0.000033Maximum Recommended Continuous Service Temperature最高连续使用温度85Coefficient of Thermal conductive导热系数BTU/HR(FT2)(0F/IN)1.4Specific Heat比热BTU/LB0F0.35Flammability Burning Rate)燃烧率D635IN/MIN1.3Water Absorption (Wt. Gainon Immersion for 24 Hrs.)吸水率D570%0.3Soluble Matter lost After Immersion浸水损耗%0.1Intemal Strain内应力D702%2Taste味觉None 无4化学性能表：25时在试剂中浸泡7天后增重试剂Reagent浓度Concentretion增重%Weight Gain%外观变化Change in AppearenceHydrochloric acid盐酸10%0.3None不变Hydrochloric acid盐酸比重1.19-0.04None不变Nitric acid硝酸40%9.7None不变Nitric acid硝酸比重1.42Dissolved被溶解Sulfuric acid硫酸30%0.19None不变Sulfuric acid硫酸比重1.80Swollen and dissolved溶胀并溶解Hydrochloric acid氢氟酸40%20.4Swollen溶胀Acetic acid醋酸5%0.44None不变Acetic acid醋酸比重1.05Dissolved被溶解Citric acid柠檬酸10%0.46None不变Hydrogen Peroxide双氧水28%0.68None不变Oleic acid油酸-0.25None不变Chromic acid铬酸40%0.23None不变Ammonium hydroxide氨水10%0.36None不变Ammonium hydroxide氨水比重0.90.33None不变Sodium hydroxide氢氧化钠10%0.31None不变Sodium hydroxide氢氧化钠50%-0.42None不变Sodium Chloride氯化钠10%0.39None不变Sodium Carbonate碳酸钠20%0.33None不变Acetone丙酮Dissolved被溶解Aniline苯胺Dissolved被溶解Ethyl乙醇95%0.07None不变alcohol苯Dissolved被溶解Benzene四氧化碳Cracked开裂Carbon tetrachloride二乙醚0.2None不变Diethyl formemide二甲替甲酰胺Dissolved被溶解Ethyl acetate乙酸乙酯Dissolved被溶解Ethylene dichloride二氯乙烯Dissolved被溶解n-heptane正庚烷-0.03None不变iso0Octane异辛烷-0.03None不变Kerosens煤油0.01None不变Toluene甲苯Crazing裂纹Mineral oil矿物油0.03None不变olive oil橄榄油0.19None不变Transformer oil变压器油0.04None不变Turpentine松节油0.15None不变Water(distilled)蒸馏水0.43None不变Phenolio solution苯酚溶液5%3.6Swollen slightly轻微溶胀Cotton oil棉花油-0.26None不变Detergent solution清洁剂溶液0.48None不变Lacquer thinner油漆稀释剂Dissolved被溶解5板厚度公差：单位：mm 毫米板材厚度厚度公差Thickness ToleranceThicknessA级Class AB级Class BC级Class C20.500.600.702.50.500.600.7030.500.600.8040.600.700.8050.600.700.8060.700.800.9080.800.901.00100.901.101.20131.201.301.50151.401.501.60181.501.601.70201.501.601.80251.601.802.00301.802.002.206亚克力板存储、加工说明6.1 板材的储存和处理：a 在室温和通风干燥环境下储存板材，不宜将板材直接暴露于阳光、热源或潮湿处。b 在板材使用之前，切勿撕去保护膜，因为日常的灰尘及脏物会因静电而粘附于板材表面。保护膜亦使板材免于磨损及刮伤。C 避免翘曲，板材应自然平放储存，如需垂直储存，最好将板材成一个小角度存放，并在下方放置支撑物。6.2 如何避免亚克力制品变形a 安装框架须预留收缩和膨胀间隙。b 须钻椭圆形的螺孔配合螺丝锁定。c 选用弹性橡胶垫片。d 热成形可提高抗冲强度，并释放内应力。e 热成型成波浪型、钻石型和半圆形可防止亚克力板因自重下垂产生变形。f 使用大幅度亚克力板时，须增加厚度以防板材由于自重而下垂变形。6.3 使用注意事项a 普通亚克力板的热变形温度约为100，持续使用温度不宜高于85。b 亚克力板表面硬度相当于铝材，在使用或加工时应小心避免表面被刮伤。如被刮伤，可以通过抛光恢复原有的光泽表面。c 亚克力板容易产生静电，吸附灰尘。清洁时用软棉布蘸1%肥皂水擦试即可。d 亚克力浇铸板的线膨胀系数约为7x10-5m/m.K，在安装、固定亚克力板时必须要考虑留够适当的伸缩间隙。6.4 亚克力板热胀冷缩量的计算方法a 假定1000毫米长的亚克力板温度由15上升到42，热膨胀量则为：1000毫米x7x10-5(42-15)=1.89毫米b 假定1000毫米长的亚克力板温度由20降到零下30，收缩量为：1000毫米x7x10-5(20-（-30）)=3.50毫米6.5亚克力板材一般加工使用说明：机械抛光用机械抛光器抛光板材边缘，应先将板材边缘尽可能地处理平整，之后在抛光布轮上打上抛光蜡，将板材轻轻的在抛光轮上加压，均匀的来回推动。此时须注意的是，切勿将板材在抛光轮上长时间的停留，否