无机富锌底漆1500A(关西).doc

分享到 无机富锌底漆1500ASD Zinc 1500A 无机富锌底漆1500APRODUCT DESCRIPTION A solvent tupe self-curing inorganic zinc rich costing based on alkylsilicate binder& INTENDED USES产品简介 烷基硅酸脂为原料的溶剂型自干型无机富锌涂料FEATURES 产品特性 Remarksble corrosion resistance极佳的防腐性能 Outsanding resistance to impact,mechanical abrasion and organic solvent 优良的耐冲击，耐磨损和耐有机溶剂性能High-build applicability极好的厚涂施工性能Remakable heat resistance and less scorch by heat treatment优良的耐热性，热处理烧损少Good applicability by standard airless spray equipment.适用于标准无空气喷涂设备。 Coefficient of friction is higher.能够提供较高的摩擦系数。 BASIC DATA基本数据Color(s) Grey颜色 灰色Mising tatio Liquid/Powder=23/77(by wt)混合比率 液体/粉末=23/77（重量比）Solid content 87%重量固体份 Film thickness Dry:75microns/cost Wet:125 microns/cost涂装膜厚 干膜：75um/道 湿膜：125 um/道Spreading tate Theoretical:0.350/kg/75microns涂覆率 理论值：0.350千克/平方米/75um Practical:Varies depending on surface conditions, environment,application,etc. 实际值：与表面处理，外界环境，施工方法等多种因素有关。STORAGE存储Flash point Greater than20闪点 20以上Shelf life 6months储存期限 6个月Shelf tempterature -10-40储存温度 APPLICATION DATA施工数据Pot life混合使用期 Temperature()温度5102030Pot life(hrs) 混合使用期8765Application methods施工方法Airless spray,air spray,brush and roller无气涂料，空气涂料，刷涂及琨涂Airless spray无气涂料Recommended 推荐Nozzle tip喷嘴尺寸0.021-0.023Fluid pressure出口压力75-125kg/cThinning稀释比例0-5% by volume(体积比)Thinner SD Zinc 1500 Thinner稀释剂 专用稀释剂Application temperature 5-40施工温度Drying time &Overcosting interval干燥时间及涂装间隔Temperature()温度5102030Dry to touch(mins)指触干燥60603020Dry hard(hrs)半硬干燥6432Merval(hrs)最小涂装时间48484848Merval(days)最大图装时间-PAINTING SYSTEM涂装配套Applied substrates Bare steel.etc.适用底材 裸钢等Subsequent cost Epomarine EX500,EpomarineEX600, pomarine SuperEX 21,or according to the costing systems of Kansai.适用上涂 Epomarine EX500,EpomarineEX600, pomarine SuperEX 21,或参考我公司推荐配套。SURFACE PREPARATION表面处理 Remove salt and other water-soluble contaminants by fresh water hosing 用清水冲去盐分及其他水溶性污物。 Degrease according to SSPC-SP1 solvent cleaning.依照SSPC-SP1溶剂清洗标准除去油脂。 Remove weld spatter and smooth weld seams and sharp sdges.除去焊接飞溅并处理焊缝，毛刺使用其光顺。 Remove rust,mill-scale and damaged shop primer by blasting to ISO Sa2.5(SSPC-SP10) or by power tooling to ISO St3.用喷砂方式除去铁锈，氧化皮和损坏的车间底漆达到ISO Sa2.5(SSPC-SP10)或用动力工具处理表面达到ISO St3. Remove dust and dirt by highpressure air