焊接工艺评定报告中英.doc

焊 接 工 艺 评 定 报 告Assessment report of welding process 报告编号： Report number评定日期： Assessment date：编 制： Compiled by审 核: Reviewed by批 准: Approved by天津赛象科技股份有限公司Tianjin Saixiang Technology Co., Ltd目 录Contents of table1. 焊接工艺评定报告Assessment report of welding process2. 焊接工艺指导书 Welding process guidance3. 外观、金相、无损检测报告 Inspection report of appearance, metallography and non-wearing4. 理化、性能试验检测试验报告 Inspection report of physical and performance test5. 母材材质检测报告 Inspection report of base material6. 焊材材质检测报告 Inspection report of welding material7. 保护气体检测报告 Inspection report of protection air 焊接工艺评定报告PQR 共 3 页 第 1 页 Assessment report of welding process PQR Sheet 3 Page 1焊接工艺评定报告编号： 考试监督机构： Number of assessment report Number of assessment report 单位名称： 天津赛象科技股份有限公司 代号：Company： Tianjin Saixiang Technology Co., Ltd Code: 地址：天津市新技术产业园区(环外)发展四道九号 焊接工艺指导书编号：Address：No.9 Hitech Developing RD. (huanwai), New Technology Industry Part, Tianjin Number of welding process guidance考试标准： 焊接日期：Reference standard for examination Date of welding：焊接方法 机械化程度: Welding type Mechanization degree接头简图：（坡口形式、尺寸、衬垫、每种焊接方法或焊接工艺、焊缝金属厚度）Sketch of joint:（Skive type, size, backing, welding type or process, thickness of metal for welding line）母材： 材料标准： Base metal: Standard：钢 号： Q345D Steel number：类、组别号： 1.2 与类、组别号： 1.2 相焊Welding between Sort/category： and sort/category厚度（mm）： 6 Thickness规格： 60*60*6 L=500（45）；100606 L=200 Size： 其他： Other:焊后热处理：Heating treatment of postwelding：热处理温度（）： 保温时间（h）： 保护气体：气体种类 混合比 流量（L/min）保 护 气 混合 80%Ar+20%CO2 18-20 尾部保护气 背面保护气 填充金属：焊材标准： GB/T8110 焊材牌号： ER50-6 焊材规格： 0.8 焊缝金属厚度： 焊缝有效厚度： 金属过渡形态：短路过渡其他： 电特性：电流种类： 直流 极性： 反接 钨极尺寸： 焊接电流（A）： 190 -220A 电弧电压：（V） 22-26 其他： 焊接位置：对接焊缝位置： 方向：（向上、向下）角焊缝位置： H-L045 方向：（向上、向下） 技术措施：焊接