三种硬度对照表

1、抗拉强度（N/mm2）维氏硬度HV布氏硬度HB洛氏硬度HRC2508076.0-2708580.7-2859085.2-3059590.2-32010095.0-33510599.8-350110105-370115109-380120114-400125119-415130124-430135128-450140133-465145138-480150143-490155147-510160152-530165156-545170162-560175166-575180171-595185176-610190181-625195185-640200190-660205195-67521019

2、9-690215204-705220209-720225214-740230219-755235223-77024022820.378524523321.380025023822.282025524223.183526024724.085026525224.886527025725.688027526126.490028026627.191528527127.893029027628.595029528029.296530028529.899531029531.0103032030432.2106033031433.3109534032334.4112535033335.51115360342

3、36.6119037035237.7122038036138.8125539037139.8129040038040.8132041039041.8135042039942.7138543040943.6142044041844.5145545042845.3148546043746.1152047044746.91555480(456)47.71595490(466)48.41630500(475)49.11665510(485)49.81700520(494)50.51740530(504)51.11775540(513)51.71810550(523)52.31845560(532)53

4、.01880570(542)53.61920580(551)54.11955590(561)54.71995600(570)55.22030610(580)55.72070620(589)56.32105630(599)56.82145640(608)57.32180650(618)57.866058.367058.868059.269059.770060.1精品资料72061.074061.876062.578063.380064.082064.784065.386065.988066.490067.092067.594068.0硬度试验是机械性能试验中最简单易行的一种试验方法。为了能用硬度

5、试验代替某些机械性能试验，生产上需要一个比较准确的硬度和强度的换算关系。实践证明，金属材料的各种硬度值之间，硬度值与强度值之间具有近似的相应关系。 因为硬度值是由起始塑性变形抗力和继续塑性变形抗力决定的，材料的强度越 高，塑性变形抗力越高，硬度值也就越高。三、硬度換算公式1. 肖氏硬度（HS）=勃式硬度（BHN）/10+122. 肖式硬度（HS）=洛式硬度（HRC）+153. 勃式硬度（BHN）=洛克式硬度（HV）4. 洛式硬度（HRC）=勃式硬度（BHN）/10-3硬度測定範圍：HS100HB500HRC70HV1300硬度換算表HVHRCHBSHVHRCHBSHVHRCHBS9406856

6、05330029.828492067.555052.350529529.22809006754051.749629028.527588066.453051.148828527.827086065.952050.548028027.126584065.351049.847327526.426182064.750049.146527025.62568006449048.445626524.825278063.348047.74482602424776062.547046.944125523.124374061.846046.143325022.22387206145045.342524521.323370060.144044.541524020.322869059.743043.64052301868059.242042.739722015.767058.841041.838821013.466058.340040.83792001165057.839039.83691908.564057.338038.8360180663056.837037.7350170362056.336036.6341160061055.73503