压力疲劳实验报告

1、测试报告序列号:11YLPL压力疲劳试验报告Test Report on Pressure Fatigue样件名称(Sample Name)委托部门(Clie nt)注意事项DECLARATION1. 未经研发部书面同意，不得部分地复制本报告。This test report shall not be duplicated without prior written approval of the R&D department.2. 报告无测试人员，审核，批准人签名无效。The report is invalid in case of no signatures of inspector, r

2、eviewer and approver.3. 报告涂改无效。The report is invalid in case of sign of erasure.4. 委托检验结果仅对所检验样品有效。Inspection result only bears responsibility for the received sample in case of commissioned inspection.样品型号Sample model申请单编号Applicatio n NO.YLPL产口口编号Product NO.委托单位Clie nt设计压力(MPa)Desig n pressure测试压力(

3、MPa)Test pressure试验依据Test sta ndard板片材料Plate material板片厚度(mm)Plate thick ness生产厂家Supplier钎焊材料Brazing material材料厚度(mm)Material thick ness生产厂家Supplier高度(mm)Height宽度(mm)Width厚度(mm)Thick ness接样日期Recepti on date完成日期Finish date测 试 目的Testproposal可对波型，板型，片距，接管及角孔尺寸，分配器，垫片，加强板等情况进行描 述。Others: Adding descript

4、ion in structure parameter, performanee draw in gs, and so on.parameter,样 品 描 述接管”外螺纹Connection, ” external threadSample descripti on测 试 条 件测试结果I或偏离分们试验装置Test equipme nt试验环境温度(oC)Ambient temperature 升压时间(s)High pressuretime 降压时间(s)Low pressure time加载波型Load curve正弦波Sine Wave压力疲劳测试台Pressure fatigue te

5、st rig 试验介质温度(oC) 20Medium temperature 上限压力(MPa) 3.0 High pressure下限压力(MPa) 0 Low pressure另一侧压力(MPa) 0 Pressure of ano ther side试验用介质Medium循环速率20Cycle rate 保压时间(s) Remai n pressure time 保压时间(s)Remai n pressure time疲劳实验压力(MPa)pressure fatiguetest pressure压力循环实测压力 -时间曲线 Pressure fatigue test graph, pressure vs timeTest con ditioaDM PTUSOepTest process record 测试侧:Q3-Q4Test side: Q3-Q4循环/次，未/内漏。cycles, not/in ter nal leakage.an alysis签发日期Rel