氯化钾镀锌故障

1、【经验交流】 氯化钾镀锌故障处理 奚兵 （常州市荆川里新村12 丙201，江苏常州 213015） 摘要：汇总了氯化钾镀锌的常见故障，包括镀层不光亮、发 雾、结合力差、烧焦、黑色条纹、厚度不均、脆性、沉积速度 慢、分散能力差、镀液浑浊等。介绍了这些疵病的产生原因及 其处理方法。提出了应加强工艺管理、认真做好镀液维护、定 期进行净化等措施，以期避免或减少故障发生。 关键词：镀锌；氯化钾；故障处理 中图分类号：TQ153.15 文献标识码：B 文章编号：1004 227X (2007 05 0028 03 Trouble shooting for potassium chloride zinc p

2、lating XI Bing Abstract: Some common problems in potassium chloride Zn plating were summarized, such as matt deposit, hazy deposit, poor adhesion, burning, black stripes, nonuniform thickness, brittleness, low deposition rate, poor throwing power and turbid bath. The causes and remedies were introdu

3、ced. Some measures should be taken to eliminate the occurrence of problems, such as strengthening process management and regular purification. Keywords: zinc plating; potassium chloride; trouble shooting Authors address: Flat.201, The Third Unit, No.12 Building, Jingchuanli Xincun, Changzhou 213015,

4、 China 1 前言 氯化钾镀锌是由最早的无氰氯化铵镀液发展而来 的一种无铵弱酸性光亮镀锌工艺。其优点是：（1）镀 液导电性好，槽压低，节省电能；（2）镀层结晶细致、 光亮、平整；（3）电流效率高，沉积速度快；（4）镀 液分散能力好；（5）适用于铸件直接电镀；（6）废水 处理简便，解决了环境污染的问题。因此，氯化钾镀 锌在工业上得到了广泛应用。 收稿日期：20061228 作者简介：奚兵（1935），男，江苏苏州人，长期从事表面处理工作。 作者联系方式：(Email xiaoxi 。 但是，在日常生产中难免会发生质量故障，主要 原因在于镀液维护不力，组分失调或受到有害杂质干 扰，以及工件前处

5、理不良。本文拟就氯化钾镀锌中常 见故障的产生原因及其处理方法进行汇总和介绍。 2 各种常见故障的产生原因及其处理方法 2. 1 镀层不光亮 2. 1. 1 产生原因 (1 镀液浓度过低（即氯化锌、氯化钾和硼酸的 含量均低）； (2 光亮剂不足； (3 pH 过高； (4 镀液温度过高； (5 阴极电流密度小； (6 金属铁杂质多； (7 有机杂质多。 2. 1. 2 处理方法 (1 通过分析，补加氯化锌、氯化钾和硼酸至工 艺规范； (2 适当添加光亮剂； (3 用稀盐酸溶液调节pH 至工艺规范； (4 降低镀液温度至工艺规范； (5 适当提高阴极电流密度； (6 加入0.5 2 mL/L 的双氧水（w = 30%），充 分搅拌后，用w = 5% 的氢 外，铁杂质还会引 起低电流密度区镀层发黄、硝酸出光变灰以及钝化后 出现蓝色或黑色污斑等不良现象；铜、铅杂质过多， 也会造成镀层钝化后