水泥体积安定性检测

肖丹相辅相成技术兴安水泥体积安定性检测

课程任务对某工地承重结构用水泥送检，请根据相关标准和规范进行水泥体积安定性检测。课程引入水泥的体积安定性，是指水泥在凝结硬化过程中，体积变化的均匀性。水泥安定性的测定方法有雷氏法（标准法）和试饼法（代用法）两种，当两种方法发生争议时以雷氏法测定的结果为准，具体检测方法参见《水泥标准稠度用水量、凝结时间、安定性检测方法》GBT1346。检测工具准备01JIANCHAEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHSEHS1.沸煮箱

图煮沸箱检测工具准备01JIANCHA2.雷氏夹

图雷氏夹检测工具准备01JIANCHA3.雷氏夹膨胀测定仪

图雷氏夹膨胀测定仪标尺最小刻度为0.5㎜。检测工具准备01JIANCHA4.湿气养护箱

图湿气养护箱温度控制在（20±1）℃，相对湿度＞90%。检测工具准备01JIANCHA5.水泥净浆搅拌机

图水泥净浆搅拌机检测工具准备01JIANCHA6.量筒：最小刻度0.1mL，精度1%

图量筒检测工具准备01JIANCHA7.天平：最大称量不小于1000g，分度值不大于1g。

图天平试样制备02ZHIBEI1.水泥标准稠度净浆的制备：按标准稠度用水量测定方法制成标准稠度的水泥净浆。2.测定前的准备工作：每个试样需成型两个试件，每个雷氏夹应配备边长或直径约80㎜、厚度4㎜～5㎜的玻璃板两块，一垫一盖。凡是与水泥净浆接触的玻璃板和雷氏夹内表面都要稍稍涂上一层油。试样制备02ZHIBEI3.雷氏夹试件的成型将预先准备好的雷氏夹放在已稍涂油的玻璃板上，并立即将已制备好的标准稠度净浆一次装满雷氏夹，装浆时一只手轻轻扶持雷氏夹，另一只手用宽约25㎜的小刀插捣3次，然后抹平，盖上稍涂油的玻璃板，接着立即将试件移至湿气养护箱中养护（24±2）h。试样制备02ZHIBEI4.试饼的成型：将制好的标准稠度净浆放在涂过油的玻璃板上，轻轻振动玻璃板并用湿布擦过的小刀由边缘向中央抹动，做成直径70～80㎜、中心厚约10㎜、边缘渐薄、表面光滑的试饼，接着将试饼放入湿气养护箱中养护（24±2）h。调整好沸煮箱内的水位，使水能保证在整个沸煮过程中都超过试件，不需中途增加试验用水。同时又能保证在（30±5）min内升至沸腾。试验步骤03BUZHOU1.沸煮试验步骤03BUZHOU当用雷氏法测定时，脱去玻璃板取下试件，先测量雷氏夹指针尖端间的距离（A），精确至0.5㎜。接着将试件放入沸煮箱水中的试件架上，指针朝上，试件之间互不交叉，然后在（30±5）min内加热至沸并恒沸（180±5）min。2.雷氏法当用试饼法测定时，脱去玻璃板取下试饼，应先检查试饼是否完整，如已开裂、翘曲，要检查原因，确认无外因时，该试饼已属不合格，不必沸煮。在试饼无缺陷的情况下，将试饼放在沸煮箱水中的篦板上，在（30±5）min内加热至沸并恒沸（180±5）min。试验步骤03BUZHOU3.试饼法沸煮结束后，立即放掉沸煮箱中的热水，打开箱盖，待箱体冷却至室温，取出试件进行判定。试验结果及评定04PINGDING1.雷氏夹法测量雷氏夹指针尖端之间的距离（C），准确至0.5㎜。当两个试件沸煮后增加距离（C－A）的平均值不大于5.0㎜时，即认为该水泥的安定性合格。当两个试件沸煮后增加距离（C－A）的平均值大于5.0㎜时，应用同一样品立即重作一次试验，若结果再如此，则认为该水泥的安定性不合格。2.试饼法试验结果及评定04PINGDING目测试饼未发现裂缝，用钢直尺检查也没有弯曲（使钢直尺和试饼底部紧靠，以两者间不透光为不弯曲）的试饼为安定性合格，反之为不合格。当两个试饼的判定结果有争议时，该水泥的安定性不合格。思考小结05XIAOJIE若水泥硬化后体积变化不均匀，即所谓的安定性不良。使用安定性不良的水泥会造成构件产生膨胀性裂缝，降低建筑物质量，甚至