铜材规格导电特性对比文件

1、磷青铜-黄铜等材料性能规格磷青铜(Phosphor Bronze)特性及规格一览表:(1) 化学成份(Chemical Composition)口王编勺化学成份(wt. %)Material DesignationCuSnPPbFeZnC5111Rem.3.54.50.030.35< 0.05< 0.10< 0.30C5102Rem.4.25.50.030.35< 0.05< 0.10< 0.30JISC5191Rem.5.57.00.030.35< 0.05< 0.10< 0.30C5212Rem.7.09.00.030.35< 0

2、.05< 0.10< 0.30(2) 物理特性(Physical Properties)口王编与(Alloy No.)密度(Density ) g/cm3弹性系数(Modulus ofElasticity )(Young ' s Modulus)GPa热膨胀系数(Coefficient of Thermal Expansion at 20oC to300 oC) Pm/m . K热传导系数(Thermal Conductivity at 20 oC) W/m . K导电率(ElectricalConductivity at 20oC)%IACSC51118.8611017.

3、883.819C51028.8611017.869.215C51918.8411018.065.814C52128.8011018.262.312(3) 机械性质(Mechanical Properties)固溶热处理，冷加工至1/8硬(1/8H);固溶热处理，冷加工至硬态 (H);沉淀硬化(AT); 1/4硬和沉淀热处理(1/4HT);半硬和沉淀热处理(1/2HT)0:退火(软)状态； H:加工硬状态；EH:特硬状态；SH:抗拉强度最大的加工制品；口釜编方Alloy No.质别Temper符号Symbol抗拉试Tensile test厚度Thickness(mm)验抗拉强度Tensile s

4、trength (kgf/mm 2)延伸率(50mm)Elongation(in2”)(%)硬度试验Hardness testHvThickness >0.15 mmC5111OC5111R-O> 0.2> 30> 38-H/4C5111R-H/4> 0.23845> 28120150H/2C5111R-H/2> 0.24252> 181301603/4HC5111R-3/4H> 0.24858> 10150170HC5111R-H> 0.25058> 8170190EHC5111R-EH> 0.2> 58&g

5、t; 5> 190C5102OC5102R-O> 0.2> 31> 40-H/4H/2C5102R-H/4C5102R-H/2> 0.2> 0.238484858> 28> 181201501501703/4HC5102R-3/4H> 0.25058> 10170190HC5102R-H> 0.25868> 8190210EHC5102R-EH> 0.2> 63> 5> 210Mechanical Properties (continuous)口釜编方Alloy No.质别Temper符号Symbo

6、l抗拉试验Tensile test硬度试验Hardness test厚度Thickness(mm)抗拉强度Tensile strength (kgf/mm 2)延伸率(50mm)Elongation(in 2 (%)Hv”)Thickness >0.15mmC5191OCC5191R-O> 0.2> 32> 42-H/4C5191R-H/4> 0.24052> 35120150H/2C5191R-H/2> 0.25060> 201501703/4HC5191R-3/4H> 0.25262> 18170190HC5191R-H>

7、0.26070> 10190210EHC5191R-EH> 0.26575> 8210230SHC5191R-SH> 0.2> 75> 5230270C5212OCC5210R-O> 0.2> 35> 45-H/4C5210R-H/4> 0.24052> 40120150H/2C5210R-H/2> 0.25060> 301501703/4HHC5210R-3/4HC5210R-H> 0.2> 0.252626072> 20> 12170190190210EHC5210R-EH> 0.2

8、7080> 8210230SHC5210R-SH> 0.2> 75> 5230270黄铜(Brass)特性及规格一览表:化学成份(Chemical Composition)口王编p化学成份(wt.%)Material DesignationCuZnFePbC260068.571.5Rem.0.05(max)0.07(max)JISC268064.068.5Rem.0.05(max)0.15(max)C280159.063.0Rem.0.05(max)0.30(max)(2)物理特性(Physical Properties)口王编亏(Alloy No.)密度(Densit

9、y )/ 3 g/cm弹性系数(Modulus ofElasticity )(Young ' s Modulus)GPa热膨胀系数(Coefficient of Thermal Expansion at 20 oC to 300 oC)岳/m . K热传导系数(Thermal Conductivityat 20 oC)W/m . K导电率(ElectricalConductivity at 20oC)%IACSC26008.5311019.912028C26808.4710520.311627C28018.3910520.812328(3)机械性质(Mechanical Propert

10、ies)合金编号AlloyNo.质另uTemper符号Symbol抗拉试验Tensile test硬度试验Hardness test厚度Thickness(mm)抗拉强度Tensile strength(kgf/mm 2)延伸率(50mm)Elongation(in 2(%)Hv')Thickness >0.15m mC2600OC2600R-O> 0.2> 28> 407090H/2C2600R-H/2> 0.23645> 28110130HC2600R-H> 0.24255-140160EHC2600R-EH> 0.25360-160

11、180SHC2600R-SH> 0.2> 58-> 180C2680OC2680R-O> 0.2> 28> 407090H/2C2680R-H/2> 0.23646> 28110130HC2680R-H> 0.24255-140160EHC2680R-EH> 0.25360-160180SHC2680R-SH> 0.2> 58-> 180C2801OC2801R-O> 0.2> 33> 35-H/4H/2C2801R-H/4C2801R-H/2> 0.2> 0.236454250>

12、 25> 1595115115140HC2801R-H> 0.2> 48-> 14018C194合金(HSM Copper)特性及规格一览表:化学成份(Chemical Composition)口王编与化学成份(wt.%)Material DesignationCuFePZnPbJISC194Rem.2.102.600.0150.150.050.20<0.03(2)物理特性(Physical Properties)口王编与(Alloy No.)密度(Density ) g/cm3弹性系数(Modulus ofElasticity )(Young ' sMo

13、dulus)GPa热膨胀系数(Coefficient of Thermal Expansion at 20 oC to 300 oC) Pm/m . K热传导系数(Thermal Conductivity at 20 oC) W/m . K导电率(ElectricalConductivity at20oC)%IACSC1948.8312116.326265(3)机械性质(Mechanical Properties)合金编 号质别Temper符号Symbol抗拉试验Tensile test硬度试验Hardness testAlloyNo.厚度Thickness(mm)抗拉强度Tensile st

14、rength (kgf/mm 2)延伸率(50mm)Elongation(in 2 (%)Hv”)Thickness>0.15mmOC194R-O> 0.23138> 2590115C194H/2C194R-H/2> 0.23744> 6115135HC194R-H> 0.24249> 3125145EHC194R-EH> 0.24751> 2135150SHC194R-SH> 0.24953-140155ESHC194R-ESH> 0.25156-145160红铜(Copper)特性及规格一览表:化学成份(Chemical C

15、omposition)口王编p化学成份(wt.%)Material DesignationCuPC1100(ETP)99.9(min)-JISC1200(DLP)99.9(min)0.0040.012C1220(DHP)99.9(min)0.0150.040(2)物理特性(Physical Properties)口王编与(Alloy No.)密度(Density)g/cm3弹性系数(Modulus ofElasticity )(Young' s Modulus)GPa热膨胀系数(Coefficient of Thermal Expansion at 20 oC to 300 oC)收/

16、m . K热传导系数(Thermal Conductivityat 20 oC)W/m . K导电率(ElectricalConductivity at 20oC)%IACSC11008.9411716.9391.1101C12008.9411716.9386.098C12208.9411717.1339.285(3)机械性质(Mechanical Properties)口釜编方Alloy No.质别Temper抗拉试验Tensile test硬度试验Hardness test厚度Thickness(mm)抗拉强度Tensile strength(kgf/mm 2)延伸率(50mm)Elong

17、ation(in 2” ) (%)HvThickness >0.15mmO> 0.2< 27> 30< 65H/4> 0.22430> 136080C1100H/2> 0.22633> 107090C12003/4H> 0.22935> 580100C1220H> 0.23037> 490110EH> 0.23340> 395110SH> 0.23541> 2100125磷青铜(Phosphor Bronze)合金各规格对照表规格名称SPEC合王编勺Alloy No.化 学成分 Chemica

18、l Composition (wt.%)规格编pSpec no.CuSnPFeNiPbZnOthersISOCuSn 4Rem.3.54.50.010.40M 0.1M 0.3M 0.05M 0.3427CuSn 54.55.5CuSn 65.57.5CuSn 87.59.0CNSC5101Rem.3.05.50.030.35Cu + Sn + PM99.59503H3112C51915.57.0C52127.09.0JISC51113.54.50.030.35Cu + Sn + PM99.5H3110C51024.55.5C51915.57.0C5212Rem.7.09.0C52107.09

19、.0M 0.1M 0.05M 0.2Cu + Sn + PM99.7H3130ASTMC511003.54.90.030.35M 0.1M 0.05M 0.3B103C510004.25.8C51900Rem.5.07.0C521007.09.0M 0.2DINCuSn 4Rem.3.54.50.010.35M 0.1M 0.3M 0.05M 0.3M 0.217662CuSn 65.57.5CuSn 87.58.5BSPB101Rem.3.54.50.020.40M 0.02M 0.32870PB1024.55.5PB1035.57.5铜合金板材厚度公差(Thickness toleranc

20、es for strip):红铜(C1100、C1200、C1220)黄铜(C2600、C2680、C2801)宽度Width厚度 Thickness厚度公差ToleranceJIS Standard (H3100)S&TM 200 mm=300 mm=400 mmM 700 mm=400 mmover 0.10 mm to 0.15 mm incl.±3.010 mm±0.020 mm±0.020 mm坦008 mmover 0.15 mm to 0.25 mm incl.±3.020 mm±0.020 mm±0.020 m

21、m±0.030 mm±0.010 mmover 0.25 mm to 0.35 mm incl.±0.020 mm±0.030 mm±0.030 mm±0.040 mm±0.010 mmover 0.35 mm to 0.50 mm incl.d0.030 mm±0.030 mm±0.040 mm±0.050 mm±0.012 mmover 0.50 mm to 0.80 mm incl.切.030 mm±0.040 mm±0.050 mm±0.060 m

22、m±0.015 mmover 0.80 mm to 1.20 mm incl.±0.040 mm±0.050 mm±0.060 mm±0.070 mm±0.020 mmover 1.20 mm to 2.00 mm incl.知.050 mm±0.060 mm±0.070 mm±0.080 mm±0.025 mmover 2.00 mm to 3.00 mm incl.也.060 mm±0.070 mm±0.080 mm±0.100 mm也.040 mm磷青铜(C2

23、600、C2680、C2801)特殊铜合金 (C194)宽度Width厚度 Thickness厚度公差ToleranceJIS Standard (H3100)S&T=400 mm=400 mm400 650 mmover 0.10 mm to 0.15 mm incl.±0.010 mm±0.008 mmover 0.15 mm to 0.25 mm incl.±0.015 mm±0.010 mmover 0.25 mm to 0.40 mm incl.±0.020 mm±0.010 mmover 0.40 mm to 0.

24、55 mm incl.±0.025 mm±0.045 mm±0.012 mmover 0.55 mm to 0.70 mm incl.±0.030 mm±0.050 mm±0.015 mmover 0.70 mm to 0.90 mm incl.±0.035 mm±0.060 mm±0.015 mmover 0.90 mm to 1.20 mm incl.+0.040 mm±0.070 mm±0.020 mmover 1.20 mm to 1.50 mm incl.±0.04

25、5 mm+0.080 mm±0.025 mmover 1.50 mm to 2.00 mm incl.±0.050 mm±0.090 mm±0.025 mm铜合金板材宽度公差(Width tolerances for strip):宽度Width厚度 Thickness厚度公差ToleranceJIS Standard (H3100)S&T=100 mmM 200 mm=100 mmM 200 mm0.10 0.55 mm.±0.10 mm±0.20 mm±0.05 mm±0.10 mm0.55 2.00m

26、m.±0.20 mm±0.30 mm±0.10 mm±0.20 mm铜合金板材蛇弯度公差(Permissible max. value on camber):宽度Width公差 Tolerance (per 1000 mm)over 6 mm to 9 mm inc9 mm max.over 9 mm to 13 mm incl.6 mm max.over 13 mm to 25 mm incl.4 mm max.over 25 mm to 50 mm incl.3 mm max.over 50 mm to 100 mm incl.2 mm max.ov

27、er 100 mm1 mm max.* Dimensional tolerances shall be in accordance with JIS H3100Direction of RollingW=Width of Strip合金种类丹铜、黄铜C2100C2200C2300C2400C260SC2600C2680化性成份(%)铜:94.096.0锌:余量铜:89.091.0锌:余量铜:84.086.0锌:余量铜:78.581.5锌:余量铜:70.573.5锌:余量铜:68.571.5锌:余量铜:64.068.0锌:余量比重(gm/cm 3)8.868.808.758.678.538.53

28、8.50热膨胀系数(10-6/C)18.118.418.719.119.919.920.3热传导系数(Cal/cm 2/cm/sec/ C )0.560.450.380.330.290.290.29导电率(%IACS,20 C)M56M 44M 37M 32M 25M 25M 24抗张强度(N/mm 2)烧炖软化M205M 225M 245M 255M 295M 295M 2951/4H2503052753352953652953753304153304153304151/2H2703452953653103853204053704403704403704403/4H-410470410470

29、410470HM280M 320M 340M 375430510430510430510EH-510610510610510610SH-565630565630565630ESH-610725610725610725伸长率(%)烧炖软化M33M 35M 40M 44M 45M 45M 451/4HM23M 25M 28M 30M 40M 40M 401/2HM 18M 20M 23M 25M 30M 30M 303/4H-M 20M 20M 20H-M 14M 14M 14EH-M 8M 8M 8SH-M 5M 5M 5ESH-硬度(Hv)烧炖软化M65M 70M 70M 80M 90M 90

30、M 901/4H658070957095751059010590105901051/2H8010095120951201001301051301051301051303/4H-130145130145130145HM 100M 120M 120M 125145160145160145160EH-160175160175160175SH-175190175190175190ESH化温度(C)-弹性系数(KN/mm 2 )118118118110110110103合金种类丹铜、黄铜Corson 合金C2720C2801C7025C7026化性成份(%)铜:6

31、2.064.20锌:余量铜:59.062.0锌:余量铜:余量锌:2.24.2硅:0.251.2镁:0.050.3铜:余量锌:1.03.0硅:0.20.7镁:0.050.3比重(gm/cm 3)8.458.398.828.9热膨胀系数(10-6/C)20.620.817.318.0热传导系数(Cal/cm 2/cm/sec/ C)0.300.290.40.37导电率(%IACS, 20 C)M26M 23M 40M 40抗张强度(N/mm 2)烧炖软化M295M 3206207555906551/4H330415350440-1/2H3704404104906558256757453/4H410

32、470-685860725795H430510M 450795900755835EH510610-SH565630-ESH610725-伸长率(%)烧炖软化M45M 35M 10M 251/4HM40M 25-1/2HM30M 15M 7M 73/4HM20-M 5M 5HM 14-M 1M 1EHM8-SHM5-ESH-硬度(Hv)烧炖软化M 90-1802101702001/4H9010585105-1/2H1051301051302002301902203/4H130145-220250210240H145160M 130240270230260EH160175-SH175190-ESH

33、190210-软化温度(C)-弹性系数(KN/mm 2 )103103132130合金种类红铜C1010(OFE)1020(OFC)C1100-PC1100(ETP) (DLCP)C1201(DLP)C1220(DHP)C1221(DHHP)化性成份(%)铜:M 99.95氧三0.0010铜 M 99.95氧三0.0010铜:M 99.90氧:0.020.045铜:M 99.90磷三0.0045氧:0.0020.006铜:M 99.90磷:0.0040.015铜:M 99.90磷:0.0150.04铜:M 99.750磷:0.0040.040比重(gm/cm 3)8.948.948.948.9

34、48.948.948.94热膨胀系数(10-6/C)17.717.717.717.717.717.717.7热传导系数(Cal/cm 2/cm/s ec/ C)0.9340.9340.9350.9340.870.810.81导电率(%IACS, 20 C)M 101M 101M 100M 99M 95M 80M 70杭张强度(N/mm 2)#炖软化M 195M 195M 195M 195M 195M 195M 1951/4H2152552152552152552152552152552152752152751/2H2553152553152553152553152553152553152553

35、153/4H-HM 290M 290M 290M 290M 290M 290M 290EH-SH-ESH-伸长率(% )#炖软化M 35M 35M 35M 35M 35M 35M 351/4HM 25M 25M 25M 25M 25M 25M 251/2HM 15M 15M 15M 15M 15M 15M 153/4H-M 5M 5M 5M 5M 5M 5-SH-ESH-硬度(Hv )庭炖软化M 605065M 60M 60M 60506550651/4H551006090608060806080609060901/2H751208510580100801008010085105851053/

36、4H-HM 80M 100100 130100 130100 130M 100M 100EH-SH-ESH-软化温度.(C)200 C200 C-弹性系数(KN/mm 2 )118118118118118118118合金种类高性能铜合金、引线架材C1040(P)C1070(P)C151C19210C194C1441化性成份(%)铜+银M 99.99氧:0.0020.006银:0.0250.035(磷:三 0.003)铜 + 银M 99.99氧:0.0020.006银:0.0860.103(磷:三 0.003)铜:M 99.82 错:0.050.15铜:M 99.6铁:0.050.15磷:0.0

37、250.04铜:M 97铁:2.12.6磷:0.0150.15锌:三0.2铜:余量.锡:0.100.20磷:0.0030.024比重(gm/cm 3)8.948.948.948.948.838.90热膨胀系数(10-6/C)17.017.017.717.717.617.7热传导系数(Cal/cm 2/cm/se c/ C )0.9270.9270.860.830.6250.81导电率M 100( M 98)M 100( M 98)M 90M 85M 60M 85(% IACS, 20 C)抗张强度(N/mm2)烧炖软化195255195255-255335310380M 2251/4H1/2H

38、215275245315215275245315245315290355275355295375-3654352753352953653/4H一-320385-H275345275345360435330415410485M 320EHM 310M310400455M370460505-SH一-440490-480525-ESH一-500550-伸长率(% )烧炖软化M 35M35-M30M25M 351/4HM 25M25M 13M20-M 251/2HM 15M 15M6M 10M5M 203/4H一-M5-HM 4M4M4启5M2-EHM 2M2M3-SH一-M2-ESH一-(Hv )烧

39、炖软化M 55M55-M 9090100M 701/4H55755575-90115-709051/2H75907590100115100125110130901203/4H一-105120-H9010590105115135110135125145M 120EHM 100M 100120135M 115135150-SH一-130150-140155-ESH一-M 145-软化温度(C )一360 C500 C450 C1/2H700390390 C弹性系数(KN/mm 2 )118118118118121118合金种类含锡丹铜磷青铜C4250C4250MC5050C5111C5102C51

40、91C5210化性成份(%)铜:8790.锡:1.53.0锌:余量铜:8688锡:2.54.锌:余量铜:余量.锡:1.01.7磷:0.0040.01铜:余量.锡:3.54.9磷:0.110.13铜:余量.锡:4.55.5磷:0.110.13铜:余量.锡:5.57.0磷:0.110.13铜:余量.锡:7.09.0磷:0.150.17比重(gm/cm 3)8.7 88.788.898.868.868.838.80热膨胀系数(10-6/C)18.518.517.817.817.81818.2热传导系数(Cal/cm 2/cm/sec/ C)0.290.250.490.200.170.160.15导电率(%IACS, 20 C)M 26M 24M45M20M 20M 13M 121抗张强度(N/mm 2)烧炖软化295380M 245M245M295M 300310395-1/4H34