不锈钢(GB／T1220--1992)

1、不锈钢（GBT1220-1992）  1)牌号和化学成分见表3-60。 表3-60不锈钢的牌号和化学成分牌  号化学成分(质量分数)()CSiMnPSNiCrM0其他奥氏体型1Crl7Mn6-Ni5N0.151.005.507.50O.0600.0303.50    5.5016.0018.00 N0.25lCrl8Mn8-Ni5NO.151.007.50lO.000.060O.0304.006.0017.0019.00 NO.251Crl8Mnl0-Ni5Mo3N0.101.008.512.000.060O.03

2、04.006.0017.0019.002.83.5N0.20O.301Crl7Ni70.151.002.000.035O.0306.008.0016.0018.00  lCrl8Ni9O.151.002.00O.035O.0308.0010.0017.0019.00  YlCrl8Ni90.151.002.oo0.20O.158.00lO.0017.0019.00 Y1Crl8Ni9SeO.151.002.000.20O.0608.00lO.0017.0019.00 SeO.15OCrl8Ni90.071.002.000.0350.0

3、308.0011.0017.0019.00  00Cr19NilOO.031.002.000.035O.0308.0012.0018.0020.00  OCr19Ni9N0.081.002.000.035O.0307.00lO.5018.0020.00 N0.100.25OCrl9Nil0-NbNO.081.002.00O.15O.0307.50lO.5018.0020.00NbO.15N0.15O.3000Crl8Ni10NO.0301.002.000.035O.0308.511.5017.0019.00 No.120.22lCr1

4、8Ni12O.121.002.000.035O，03010.5013.0017.0019.00  OCr23NNi130.081.002.00O.0350.03012.0015.0022.0024.00  OCr25Ni20O.081.002.00O.0350.03019.0022.0024.0026.00  OCrl7Ni-12M020.081.002.00O.035O.03010.0014.0016.0018.502.003.00 lCr18Nil2-M02T0.121.002.00O.035O.03011.0014.0

5、016.0019.001.802.50Ti5×(C 0.02)O.80OCrl8Nil2-M02TiO.081.002.00O.0350.03011.0014.0016.0019.001.80 2.50Ti5x CO.7000Crl7Ni-14M020.0301.002.000.0350.03012.0015.oo16.0018.002.003.00 OCrl7Nil2-M02NO.081.002.00O.0350.030lO.0014.0016.0018.002.003.00NO.10 O.2200Crl7Nil3-Mo2NO.0301.002.000.035O.0301

6、0.5014.5016.0018.502.003.00N0.12O.22OCrl8Nil2-M02Cu2O.081.002.00O.035O.03010.0014.5017.0019.001.202.75Cul.002.5000Cr18Nil4-M02Cu2O.0301.002.000.035O.03012.0016.0017.0019.001.202.75Cul.002.500Crl9Nil3M03O.081.002.00O.035O.03011.0015.0018.0020.003.004.00 00Crl9-Nil3M030.0301.002.00O.0350.03011.00

7、15.0018.0020.003.004.00 lCrl8Nil2-M03Ti0.121.002.00O.035O.03011.0014.0016.0019.002.503.50Ti5×(C-O.02)O.080Cr18Ni-12M03Ti 0.081.002.00O.0350.03011.0014.0016.0019.002.503.50Ti5×CO.70OCrl8Ni-16M05O.0401.002.000.0350.03015.0017.0016.0019.004.006.00 lCrl8Ni9Ti0.121.002.00O.035O.0308.0

8、011.0017.0019.00 Ti5×(C-O.02)O.80OCrl8-NilOTi 0.081.002.000.035O.0309.0012.0017.0019.00 Ti5×COCrl8Ni1lNbO.081.002.000.0350.0309.001.3017.0019.00 Nb10×COCrl8Ni9Cu3O.081.002.00O.035O.0308.5010.5017.0019.00 Cu3.004.000Crl8Nil3Si4O.083.005.002.00O.0350.03011.5015.0015.

9、0020.00 奥氏体一铁素体型0Cr26Ni5Mo20.081.001.500.035O.0303.006.0023.0028.001.003.00lCrl8Ni1l-Si4AlTiO.10  0.183.404.000.08O.0350.03010.0012.0017.5019.50 A10.100.30  TiO.400.7000Crl8Ni5-M03Si2O.0301.302.001.002.00O.0350.0304.505.5018.oo19.502.503.00 铁素体型OCrl3AlO.081.oo1.00O.0350.0301

10、1.5014.50 A10.10O.3000Crl2O.0301.001.00O.035O.03011.0013.00  1Crl7 O.12O.751.00O.035O.03016.0018.00  YlCrl7 O.120.101.250.0600.1516.0018.00 lCrl7M0 O.12O.101.000.035O.03016.0018.000.751.25 00Cr30M02O.010O.40O.40O.030O.020 28.5032.001.502.50N0.01500Cr27M0O.0lOO

11、.400.40O.0300.020 25.0027.500.751.50N0.015马氏体型lCrl2 O.150.501.000.035O.030L1.5013.00  lCrl3 O.151.001.000.035O.03013.5011.50  0Crl3O.081.001.00O.035O.03013.5011.50  YlCrl3 O.151.001.25O.060O.1512.0014.00 lCrl3M0O.08  0.180.601.00O.0350.03011.5014.000.300.

12、60 2Crl30.16  O.251.001.00O.035O.03012.0014.00  3Crl3O.26O.351.001.00O.035O.03012.0014.00  Y3Crl3O.26O.401.001.25O.0600.1512.0014.00 3Crl3M0O.280.350.801.000.035O.03012.0014.00O.501.00 4Crl30.36O.45O.600.80O.0350.03012.0014.00  1Crl7N20.110.17O.80O.8

13、00.035O.0301.502.5016.0018.00  7Crl7O.60O.751.001.000.035O.03016.0018.00 8Cr170.75O.951.001.00O.035O.03016.0018.00 9Crl80.901.00O.800.80O.0350.03017.0019.00 llCrl7O.951.201.001.00O.0350.03016.0018.00 YllCrl7O.951.201.001.250.060O.1516.0018.00 9Crl8MoO.951.100.80O.8

14、0O.0350.03016.0018.000.400.70 9Crl8MoVO.850.95O.800.80O.035O.03017.0019.001.001.30V0.07O.012沉淀硬化型OCrl7N.4-Cu4NbO.071.001.000.035O.0303.005.0015.5017.50Cu3.005.00Nb0.15O.45Ocrl7Ni7Al0.09I.001.00O.0350.0306.507.7516.0018.00CuO.50A10.751.500Cr15Ni7-M02Al0.091.001.00O.035O.0306.507.5014.0016.002.00

15、3.00A10.751.50可加入不大于0.60钼。必要时，可添加上表以外的合金元素。允许含有不大于O.60镍。    可以加入不大于0.75钼。00Cr30M02和00Cr27M0允许有不大于O.50镍，不大于0.20铜，但镍+铜不大于0.50，必要时，可添加表列以外的合金元素。除专用外，一般不推荐使用。(2)力学性能见表361表364。表3-6l经固溶处理的奥氏体和奥氏体.铁素体钢的力学性能牌  号固溶处理拉伸试验硬度试验ó0.2ó b5()()布氏硬度HBS洛氏硬度HRB维氏硬度HV MPa奥氏体型1Crl7Mn6Ni

16、5N10101120快冷2755204045241100253lCrl8Mn8Ni5N10101120快冷275520404520795218lCrl8Mnl0Ni5M03N11001150快冷3456804565   1Crl7Ni710101150快冷205520406018790200lCrl8Ni910101150快冷205520406018790200Y1Cr18Ni9lOl01150快冷205520405018790200YlCrl8Ni9Se10101150快冷205520405018790200OCrl8Ni910101150快冷205520406

17、01879020000Cr19Nil010101150快冷1774804060187902000Cr19Ni9N10101150快冷2755503550217952200Cr19Nil0NbN10101150快冷345685355025010026000Crl8Nil0N10101150快冷245550405021795220lCrl8Ni12lOl01150快7902000Cr23Nil3lOl01150快冷2055204060187902000Cr25Ni2010101180快冷<,TD wid,th="6%"> 205520405

18、0187902000Crl7Ni12Mo210101150快冷205520406018790200lCrl8Ni12M02Ti101O1100快冷205530405518790200OCrl8Ni2M02Ti10101100快冷20553040551879020000Crl7Nil4M0210lO1150快冷177480406018790200OCrl7Ni12M02N10lO1150快冷27555035502179522000Crl7Nil3M02N1O1O1150快冷245550405021795220OCrl8Ni12M02Cu21Ol01150快冷2055204060187902000

19、0Crl8Nil4M02Cu2101O1150快冷1774004060187902000Crl9Nil3M0310101150快冷20552040601879020000Crl9Nil3Mo310101150快冷177480406018790200lCrl8Nil2M03Til0001100快冷205530405518790200OCrl8Nil2M03Ti10001100快冷205530405518790200OCrl8Ni16M05j0301180快冷177480404518790200lCrl8Ni9Ti9201150快冷205520405018790200OCrl8NilOTi9201

20、150快冷205520405018790200OCrl8NillNb9801150快冷2065204050187902000Crl8Ni9Cu3lOl01150快冷177480406018790200OCrl8Nil2Si4lOl01150快冷205520406020795218奥氏体一铁素体型0Cr26Ni5M029501100快冷3905901840277292921Crl8Ni11Si4AlTi9301050快冷4407152540   00Cr18Ni5M03Si29201150快冷3905902040 30300注：1.对于OCrl8Nil0T

21、i、OCrl8NillNb、1Crl8Ni9Ti、0Crl8Nil2M02T1、OCrl8Ni一12M03Ti和1Crl8Nil2M03Ti根据需方要求可进行稳定化处理，此时的热处理温度为850930，但必须在合同中注明。      2.1Crl8Ni9Ti与Ocrl8Nil0Ti、1Crl8Nil2M02Ti与0Crl8Nil2M02Ti、lCrl8Ni一12M03Ti与OCrl8Nil2M03Ti牌号，力学性能指标一致，需方可根据耐腐蚀性能的差别来选用。      3.1Crl8NillSi

22、4AITi的冲击试验札值不小于63J。表362经退火的铁素体钢的力学性能牌号退火处理拉伸试验冲击试验硬度试验óo.2ób 5()()AKJ布氏硬度HBSMPa0Crl3A1780830空冷或缓冷17741020607818300Crl2700820空冷或缓冷1962652260 1831Cr17780850空冷或缓冷2054502250 183Y1Crl7680820空冷或缓冷2054502250 1831Cr17Mo780850空冷或缓冷2054502260 18300Cr30M029001050快冷2954502045 

23、22800Cr27Mo9001050快冷2454102045 219表3-63经退火或淬火回火的马氏体钢的力学性能牌号热处理°C退火后的布氏硬度HBS经淬回火的力学性能拉伸试验冲击试验  AKJ布氏硬度HBS退火淬火回火ó0.2ób5()()MPa1Crl2800900缓冷或约750快冷9501000油冷700750快冷20039055025551181701Crl3800900缓冷或约750快冷9501000油冷700750快冷200345540255578159OCrl3800900缓冷或约750快冷9501000油冷700750冷1833

24、454902460  YICrl3800900缓冷或约750快冷9501000油冷700750快冷2003455402555781591Crl3Mo830900缓冷或约750快冷9701020油冷650750快冷2004906852060781922Crl3800900缓冷或约750快冷920980油冷600750快冷2234406352050631923Crl3800900缓冷或约750快冷920980油冷600750快冷235540735124024217Y3Crl3800900缓冷或约750快冷920980油冷600750快冷2355407351240242173Cr

25、l3Mo800900缓冷或约750快冷10251075油冷200300油、水、空冷207     HRC504Crl3800900缓冷或约750快冷10501100油冷200300空冷20l     HRC 501Crl7Ni2680700高温回火空冷9501050空冷275350空冷285  1080 10  39 7Crl7880920缓冷10101070油冷100180空冷255   

26、60; HRC 548Crl7880920缓冷10101070油冷100180快冷255     HRC 569Crl8800920缓冷10001050油冷200300油、空冷255     HRC 55llCrl7800920缓冷10101070油冷100180快冷269     HRC 58YllCrl7800920缓冷10101070油冷100180快冷269  

27、0;  HRC 589Crl8Mo800900缓冷10001050油冷200300空冷269     HRC559Crl8MoV800920缓冷10501075油冷100200空冷269     HRC55表364经热处理的沉淀硬化型钢的力学性能牌号热处理拉伸试验硬度试验种类条  件óo.2ób5  () ()布氏硬度HBS洛氏硬度HRCMPa0Crl7Ni4-Cu4Nb固溶10201060快冷  

28、0; 36338480时效经固溶处理后，470490空冷180  1310104037540550时效经固溶处理后，540560空冷000  1060124533135580时效经固溶处理后，570590空冷865  1000134530231620时效经固溶处理后，610630空冷7259301650277280Crl7Ni7A1固溶10001100快冷380103020 229 565时效9601140525363 565时效103012304lO388 OCrl5Ni7M02A1固溶10001100快冷

29、60;   269 565时效11001210725375 510时效 12101320620388 经固溶处理后，于(760±15°C)保持90min，在1h内冷却到15以上，保持30min.再加热到(565±10)，保持90min空冷。经固溶处理后，(955±lO)保持10min，空冷到室温，在24h内冷却到(一73±60)°C，保持8h，再加热到(510±10)保持60min后空冷。(3)用途见表365。 表3-65不锈钢的特性和应用类型序号牌  号

30、特性和应用奥氏体型l1Crl7Mn6Ni5N节镍钢种，代替牌号1Crl7Ni7，冷加工后具有磁性。铁道车辆用21Crl8Mn3NiSN节镍钢种，代替牌号1Crl8Ni931Crl8Mnl0Ni5M03N对尿素有良好的耐蚀性，可制造尿素腐蚀的设备41Crl7Ni7经冷加工有高的强度，铁道车辆，传送带螺栓螺母用51Crl8Ni9经冷加工有高的强度，但伸长率比1Crl7Ni7稍差。建筑用装饰部件6Y1Crl8Ni9提高切削性，耐烧蚀性，最适用于自动车床。螺栓螺母7Y1Crl8Ni9Se提高切削性，耐烧蚀性。最适用于自动车床。铆钉、螺钉80Crl8Ni9作为不锈耐热钢使用最广泛，如食品用设备，一般化工

31、设备，原子能工业用设备900Crl9Nil0比0Crl9Ni9碳含量更低的钢，耐晶问腐蚀性优越，为焊接后不进行热处理部件类lO0Crl9Ni9N在牌号0Crl9Ni9上加N，强度提高，塑性不降低。使材料的厚度减少。作为结构用高强度部件110Crl9Nil0NbN在牌号0Crl9Ni9上加N和Nb具有与0Crl9Ni9相同的特性和用途1200Crl8Nil0N在牌号00Crl9Nil0上添加N，具有以上牌号同样特性，用途与0Crl9Ni9N相同，但耐晶间腐蚀性更好131Crl8Nil2与0Crl9Ni9相比，加工硬化性低。旋压加工，特殊拉拔，冷镦用140Cr23Nil3耐腐蚀性，耐热性均比0Cr

32、l9Ni9好150Cr25Ni20抗氧化性比0Cr23Nil3好，实际上多作为耐热钢使用160Crl7Nil2M02在海水和其他各种介质中，耐腐蚀性比0Crl9Ni9好，主要作耐点蚀材料奥氏体型171Crl8Nil2M02Ti用于抵抗硫酸、磷酸、蚁酸、醋酸的设备，有良好耐晶间腐蚀性180Crl8Nil2M02Ti用于抵抗硫酸、磷酸、蚁酸、醋酸的设备，有良好耐晶间腐蚀性1900Crl7Nil4M02为0Crl7Nil2M02的超低碳钢，比0Crl7Nil2M02耐晶问腐蚀性好200Crl7Nil2M02N在牌号0Crl7Nil2Mo2中加入N，提高强度，不降低塑性，使材料的厚度减薄。作耐腐蚀性较

33、好的强度较高的部件2100Crl7Nil3M02N在牌号00Crl7Nil4M02中加入N，具有以上牌号同样特性，用途与0Crl7Nil2M02N相司，但耐晶间腐蚀性更好。220Crl8Nil2M02Cu2耐腐蚀性、耐点腐蚀性比0Crl7Nil2M02好，用于耐硫酸材料2300Crl8Nil4M02Cu2为0Crl8Nil2M02Cu2的超低碳钢，比0Crl8Nil2M02Cu2的耐晶间腐蚀性好240Crl9Nil3M03耐点腐蚀性比0Crl7Nil2M02好，作染色设备材料等奥氏体型2500Crl9Nil3M03为0Crl9Nil3M03的超低碳钢，比0Crl9Nil3M03耐晶间腐蚀性好2

34、61Crl8Nil2M03Ti用于抵抗硫酸、磷酸、蚁酸、醋酸的设备，有良好耐晶间腐蚀性270Crl8Nil2M03Ti用于抵抗硫酸、磷酸、蚁酸、醋酸的设备，有良好耐晶间腐蚀性280Crl8Nil6M05吸取含氯离子溶液的热交换器，醋酸设备，磷酸设备，漂白装置等，在00Crl7Nil4M02和O0Crl9Nil3M03不能适用的环境中使用291Crl8Ni9Ti作焊芯、抗磁仪表、医疗器械、耐酸容器及设备衬里输送管道等设备和零件300Crl8Nil0Ti添加Ti提高耐晶问腐蚀性，不推荐作装饰部件3l0Crl8NillNb含Nb提高耐晶间腐蚀性320Crl8Ni9Cu3在牌号0Crl9Ni9中加入Cu，提高冷加工性的钢种。冷镦用330Crl8Nil3Si4在牌号0Crl9Ni9中增加Ni。添加Si，增加耐应力腐蚀断裂性。用于含氯离子环境奥氏体铁素体型340Cr26Ni5M02具有双相组织，抗氧化性，耐点腐蚀性好。具有高的强度，作耐海水腐蚀用等351Crl8Nil1Si4A1Ti制作抗高温浓硝酸介质的零件和设备3600Crl8Ni5M03Si2具有铁素体.奥氏体型双相组织，耐应力腐蚀破裂性好，耐点蚀性能与00Crl7Nil3M02相当，具有较高的强度适于含氯离子的环境，用于