关 键 词：

软管 接头 注射 模具设计 10 CAD 图纸 PDF

资源描述：

喜欢这套资料就充值下载吧。。。资源目录里展示的都可在线预览哦。。。下载后都有，，请放心下载，，文件全都包含在内，，【有疑问咨询QQ:414951605 或 1304139763】

内容简介：

英语翻译FormingForming can be defined as a process in which the desired size and shape are obtained through the plastic deformations of a material. The stresses induced during the process are greater than the yield strength, but less than the fracture strength, of the material. The type of loading may be tensile, compressive, bending, or shearing, or a combination of these. This is a very economical process as the desired shape, size, and finish can be obtained without any significant loss of material. Moreover, a part of the input energy is fruitfully utilized in improving the strength of the product through strain hardening. The forming processes can be grouped under two broad categories, namely, cold forming, and hot forming. If the working temperature is higher than the recrystallization temperature of the material, then the process is called hot forming. Otherwise the process is termed as cold forming. The flow stress behavior of a material is entirely different above and below its recrystallization temperature. During hot working, a large amount of plastic deformation can be imparted without significant strain hardening. This is important because a large amount of strain hardening renders the material brittle. The frictional characteristics of the two forming processes are also entirely different. For example, the coefficient of friction in cold forming is generally of the order of 0.1, whereas that in hot forming can be as high as 0.6. Further, hot forming lowers down the material strength so that a machine with a reasonable capacity can be used even for a product having large dimensions. The typical forming processes are rolling, forging, drawing, deep drawing, bending, and extrusion. For a better understanding of the mechanics of various forming operations, we shall briefly discuss each of these processes.Rolling In this process, the job is drawn by means of friction through a regulated opening between two power-driven roll. The shape and size of the product are decided by the gap between the rolls and their contours. This is a very useful process for the production of sheet metal and various common sections, e.g., rail, channel, angle, and round.Forging In forging, the material is squeezed between two or more dies to alter its shape and size. Depending on the situation, the dies may be open or closed.Drawing In this process, the cross-section of a wire or that of a bar or tube is reduced by pulling the workpiece through the conical orifice of a die. When high reduction is required, it may be necessary to perform the operation in several passes.Deep Drawing In deep drawing, a cup-shaped product is obtained from a flat sheet metal with the help of a punch and a die. The sheet metal is held over the die by means of a blank holder to avoid defects in the product.BendingAs the name implies, this is a process of bending a metal sheet plastically to obtain the desired shape. This is achieved by a set of suitably designed punch and die. Extrusion This is a process basically similar to the closed die forming. But in this operation, the workpiece is compressed in a closed space, forcing the material to flow out through a suitable opening, called a die. In this process, only the shapes with constant cross-sections (die outlet cross-section) can be produced.Advantages and Disadvantages of Hot and Cold Forming Now that we have covered the various types of metal working operations, it would only be appropriate that we provide an overall evaluation of the hot and cold working processes. Such a discussion will help in choosing the proper working conditions for a given situation. During hot working, a proper control of the grain size is possible since active grain growth takes place in the range of the working temperature. As a result, there is no strain hardening, and therefore there is no need of expensive and time-consuming intermediate annealing. Of course, strain hardening is advisable during some operations (viz., drawing) to achieve an improved strength; in such cases, hot working is less advantageous. Apart from this, strain hardening may be essential for a successful completion of some processes (e.g., in deep drawing, strain hardening prevents the rupture of the material around the bottom circumference where the stress is maximum). Large products and high strength materials can be worked upon under hot conditions since the elevated temperature lowers down the strength and, consequently, the work load. Moreover, for most materials, the ductility increases with temperature and, as a result, brittle can also be worked upon by the hot working operation. It should, however, be remembered that there are certain materials (viz., steels containing sulphur ) which become more brittle at elevated temperatures. When a very accurate dimensional control is required, hot working is not advised because of shrinkage and loss of surface metal due to scaling. Moreover, surface finish is poor due to oxide formation and scaling. The major advantages of cold working are that it is economical, quicker, and easier to handle because here no extra arrangements for heating and handling are necessary. Further, the mechanical properties normally get improved during the process due to strain hardening. What is more, the control of grain flow directions adds to the strength characteristics of the product. However, apart from other limitations of cold working (viz., difficulty with high strength and brittle materials and large product sizes), the inability of the process to prevent the significant reduction brought about in corrosion resistance is an undesirable feature. 成形成形可以定义为一种通过材料的塑性变形获得所需尺寸和形状的工艺。在此工艺中引起的应力大于材料的屈服强度，但小于材料的断裂强度。加载的类型可以是拉应力、压应力、弯曲应力或剪应力，或者是这些类型的组合。这是个很经济的方法，因为可以获得所需的形状、尺寸和光洁度而无需使材料有任何大的损失。此外，一部分输入的能量在通过应变硬化提高产品的强度上得到了卓有成效的利用。成形工艺可以分为以下两个大类，即冷成形和热成形。如果加工温度高于材料的再结晶温度，那么这一过程就叫热变形，否则，这一个过程就被称为冷变形。材料的流动应力在再结晶温度之上或之下全然不同。在热加工过程中，可以产生大的塑性变形而无大的冷作硬化。这一点很重要，因为大的冷作硬化会使材料变脆。两种成形方法的摩擦特性也完全不同。例如，冷成形的摩擦系数一般为0.1左右，而热变形的摩擦系数可以高达0.6。此外，热变形降低了材料的强度，结果甚至可以使用具有一定容量的机器加工很大尺寸的产品。典型的成形方法有轧制、锻造、拉延、拉深、弯曲和挤压。为了更好地理解各种成形操作地机械学原理，我们将简要讨论每一种方法。轧制在这一工艺中，通过一个调整过的位于两个动力驱动的轧辊之间的孔利用摩擦来拉伸工件。产品的形状和尺寸由轧辊及其轮廓之间的间隙来决定。这是一种很有用途的工艺，用于生产金属薄板和各种常用端面，如铁轨、槽钢、角钢和圆钢。锻造 锻造时，材料在两个和多个磨具间受到挤压以改变其形状和尺寸。根据情况不同，磨具可以是开式或闭式。拉延在这一工艺中，金属丝的截面或者是条钢或钢管的 截面由于工件被拉过磨具的锥形孔而减小。当截面需要减小很多时，也许有必要通过几个阶段来完成此操作。拉深在拉深中，杯形产品是在一个凸模和一个凹模的帮助下由一块金属板获得的。金属薄板被放在磨具上利用一个坯料压板来避免产品缺陷。弯曲如其名所示，这是一道塑性弯曲一块金属薄