一种冷加工无缝铝合金轮毂的制备方法

压力旋转法，采用铝合金板材为原料，通过多次压力旋转、拉伸、滚动、回退以及切割等过程，最终制备出了无缝的铝合金轮毂。在制备过程中，合理地控制轮毂的壁厚、直径、强度等参数，并对制备的轮毂进行了力学性能测试和应用实验。结果表明，该冷加工无缝铝合金轮毂具有轻质、高强度、耐腐蚀、低噪音等优点，为工程领域中轻量化设计提供了一种Thispaperpresentsamethodofpreparingseamlessaluminumalloywheelsbycoldworking.Themethodusesaluminumalloyplatesasrawmaterialsandemployspressurespinningprocessthatincludesmultiplepressurespinning,stretching,rolling,withdrawing,cuttingandotherprocessestofinallyproduceseamlessaluminumalloywheels.Duringthepreparationprocess,reasonablecontrolofwheelthickness,diameter,strengthandotherparameterswastaken,andthemechanicalpropertiesandapplicationexperimentsofthepreparedwheelsweretested.Theresultsshowthatthecoldworkingseamlessaluminumalloywheelshavethecharacteristicsoflightweight,highstrength,corrosionresistance,lownoise,etc.,whichprovideanewchoiceforlightweightdesigninengineeringofautomobiles.Keywords:aluminumalloy;wheel;seamless;coldworking;lightweightdesign6061铝合金板材，合金组成如下表所示。表16061铝合金组成（质量分数）成分CuMgSiFeZnMnTiCr质量分数0.15~0.40.8~1.20.4~0.80.70.250.150.04~0.35300mm×300mm×10mm，初始重量约为径为40mm的孔。500MPa40r/min20mm、滚动次数10次、回退次数2次。将初期加工的轮毂放入内径为40mm的模具中，利用挤压法600MPa30mm、速度20mm/min、滚动次数10次、回退次数2次。20mm的模具中，进行最终加工。具体工艺参数为：压力700MPa、进料长度30mm、速度20mm/min、滚动次数10次、回退次数2次。400mm，壁厚约为5mm。制品的大小、壁厚和形态可以根据实际需要进行调节。试结果显示，轮毂抗压强度达到200MPa。试结果显示，轮毂抗拉强度达到130MPa。试结果显示，轮毂抗弯强度达到170MPa。试