1、机械工程专业英语English In Mechanical Engineering,Prepared by Xiaoping Pang From College of Mechanical Engineering Chongqing University,16 Wear and Lubrication,Wear can be defined as the progressive loss of material from the operating surface of a body occurring as a result of relative motion at the surface

2、. The problem of wear arises wherever there are load and motion between surface, and is therefore important in engineering practice, often being the major types of wear are describe next:,16 Wear and Lubrication,Adhesive Wear. When two surfaces are loaded against each other, the whole of the contact

3、 load is carried on very small area of the asperity contacts. The real contact pressure at these asperities is very high, and adhesion takes place between them. If a tangential force is applied to the model shown in Fig.16.1, shearing can take place either (a) at the interface or (b) below or above

4、the interface, causing adhesive wear. Because of factors such as strain hardening at the asperity contact, the adhesive bonds often are stronger than the base metals. Thus, during sliding, fracture usually occurs in the weaker or softer component, and a wear fragment is generated. Although this frag

5、ment is attached to the harder component (upper surface in Fig. 16. 1c), it eventually becomes detached during further rubbing at the interface and develops into loose wear particle.,16 Wear and Lubrication,Abrasive Wear. This type of wear is caused by a hard, rough surface (or a surface containing

6、hard, protruding particles) sliding across another surface. As a result, microchips are produced, thereby leaving grooves or scratched on the softer surface (Fig.16.2). In fact, processes such as filing and grinding act in this manner. The difference is that, in these operations, the process paramet

7、ers are controlled to produce the desired shapes and surfaces through wear; whereas, abrasive wear generally is unintended and unwanted. Corrosive Wear. Also known as oxidation or chemical wear, this type of wear is caused by chemical or electrochemical reactions between the surfaces and the environ

8、ment. The fine corrosive products on the surface constitute the wear particles in this type of wear. When the corrosive layer is destroyed or removed through sliding, another layer begins to form, and the process of removal and corrosive layer formation is repeated.,16 Wear and Lubrication,Fatigue W

9、ear. Fatigue wear is caused when the surface of a material is subjected to cyclic loading; one example of this is the rolling contact in bearings. The wear particles usually are formed through spalling or pitting. Another type of fatigue wear is by thermal fatigue. Cracks on the surface are generate

10、d by thermal stresses from thermal cycling, such as when a cool forging die repeatedly contacts hot workpieces. These cracks then join, and the surface begins to spall, producing fatigue wear. Although wear general alters a parts surface topography and may result in severe surface damage, it also ca

11、n have a beneficial effect. The running-in period for various machines and engines produces this type of wear by removing the peaks from asperities (Fig.16.3). Thus, under controlled conditions, wear may be regarded as a type of smoothing or polishing process.,16 Wear and Lubrication,Lubrication is

12、a process by which the friction and wear between two solid surfaces in relative motion is reduced significantly by the interposing a lubricant between them. These are four types of fluid lubrication that are generally of interest in engineering practice (Fig.16.4): 1. In thick-film lubrication, the

13、two surfaces are completely separated from each other by a continuous fluid film. The fluid film can be developed either hydrostatically or, more often by the wedge effect of the sliding surfaces in the presence of a viscous fluid at the interface. 2. As the load between the two surfaces increases o

14、r as the sliding speed and viscosity of the fluid decrease, the lubricant film becomes thinner (thin-film lubrication). This condition raises the friction at the sliding interfaces and results in slight wear.,16 Wear and Lubrication,3. In mixed lubrication, although the contacting surfaces are separated by a thin lubricant film, asperity contact also may take place. The total applied load is thought to be carried by asperity contacts and partly by hydrodynamic action. 4. In boundary lubrication, the load is supported by contacting surfaces

温馨提示

  • 1. 本站所有资源如无特殊说明,都需要本地电脑安装OFFICE2007和PDF阅读器。图纸软件为CAD,CAXA,PROE,UG,SolidWorks等.压缩文件请下载最新的WinRAR软件解压。
  • 2. 本站的文档不包含任何第三方提供的附件图纸等,如果需要附件,请联系上传者。文件的所有权益归上传用户所有。
  • 3. 本站RAR压缩包中若带图纸,网页内容里面会有图纸预览,若没有图纸预览就没有图纸。
  • 4. 未经权益所有人同意不得将文件中的内容挪作商业或盈利用途。
  • 5. 人人文库网仅提供信息存储空间,仅对用户上传内容的表现方式做保护处理,对用户上传分享的文档内容本身不做任何修改或编辑,并不能对任何下载内容负责。
  • 6. 下载文件中如有侵权或不适当内容,请与我们联系,我们立即纠正。
  • 7. 本站不保证下载资源的准确性、安全性和完整性, 同时也不承担用户因使用这些下载资源对自己和他人造成任何形式的伤害或损失。

评论

0/150

提交评论