金属拉伸试验报告.docx

金属拉伸试验报告试验部门（单位）：余嫦材料名称：纯铜试验日期：2012-04-16:20-02试验标准：GB/T 228.1-2010试样形状：圆形截面试样批号：S2温度：18序号试样编号最大试验力-kN1517.043载荷-位移曲线表（一）从位移载荷曲线上选取的数据点及相应的工程应力应变数据点载荷P/kN位移s/mm0.8020.261.89.2412.6814.61215.81616.5201724172816.23214341235.21035.5835.6635.7/Mpa010.180.003225.440.028976.340.0643117.060.1286160.320.1929185.770.2572201.040.3215209.950.3858216.310.4501216.310.5144206.130.5466178.130.5659152.690.5707127.240.5723101.790.5739576.34由上表刻得出工程应力应变曲线如图图（一）工程应力应变曲线-表（二）真应力应变数据及相应的对数取值tt/Mpa010.170.000325.530.028578.550.0623124.590.1209180.940.1764221.610.2289252.750.2788277.450.3263299.770.3716313.680.4150312.180.4360275.510.4484239.100.4515199.860.4525163.860.4535120.16lntlnt-5.7413-3.6678-3.5568-2.5439-2.7753-2.0827-2.1120-1.7095-1.7349-1.5068-1.4744-1.3753-1.2772-1.2820-1.1198-1.2047-0.9897-1.1593-0.8793-1.1641-0.8299-1.2891-0.8019-1.4308-0.7950-1.6101-0.7928-1.8087-0.7905-2.1188由以上数据的得到的未经修正的真应力应变曲线图（二）有以上数据的得到的未经修正的真应力应变曲线t-t图(三) 未经修正的lnt lnt曲线A点为修正转折点（A点后发生颈缩，局部变形，需修正求真应力）表（三）经Davidenkov公式修正的真应力应变数据tt/MPa010.170.000325.530.028578.550.0623124.590.1209180.940.1764221.610.2289252.750.2788277.450.3263299.770.3716313.680.3212380.550.3786385.740.4681392.000.6938399.86由上面的数据得到t-t曲线图（三）经Davidenkov公式修正的真应力应变t-t曲线图中AB段为未经修正，BC段经Davidenkov公式修正。从上面的经Davidenkov公式修正的真应力应变t-t曲线可以看出后面的修正部分明显偏出事实，因此修正项为错误结果，得不到合符误差的真应力应变t-t曲线，不满足实验要求。从Davidenkov修正公式：a=PAi11+a4R分析来看，误差项主要来源于加载载荷与实测样品直径的不同时性造成的，即为先测出样品的直径a，过一小段时间后才读出该直径对应的载